Specification |
Feature: Good Acid Resistance, Low Thermal Conductivity;
Production Process: Extrusion;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Brick;
Sio2: 89%~92%;
Bulk Density: 0.6g/cm3~0.8g/cm3;
Fe2o3: 0.52%~0.62%;
Cold Crushing Strength: 2.5MPa~5.0MPa;
|
Feature: Good Acid Resistance, High Refractoriness, Low Thermal Conductivity, Thermal Shock Resistance, Volume Stability;
Production Process: Vibration Molding;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Pipe;
Type: Silicon Carbide Pipe;
Temperature: High;
Compation: Good;
Antiknock Characteristic: Good;
Stability: Good;
Life: Long;
|
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Low Thermal Conductivity, Thermal Shock Resistance, Volume Stability, Long Time Materials;
Production Process: Semi-Dry Pressing;
Refractoriness (℃): 1580< Refractoriness< 1770, 1770< Refractoriness< 2000;
Shape: Brick, Brick;
Type: Silica Brick, Refractory Material;
Material: Silica Sand;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 22%;
Cold Crushing Strength: 30MPa;
Refractoriness Under Load: 1640-1660;
Fe2o3: 1.0-1.4%;
Sio2: 94-96%;
|
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Low Thermal Conductivity, Thermal Shock Resistance, Volume Stability, Long Time Materials;
Production Process: Semi-Dry Pressing;
Refractoriness (℃): 1580< Refractoriness< 1770, 1770< Refractoriness< 2000;
Shape: Brick, Brick;
Type: Silica Brick, Refractory Material;
Material: Silica Sand;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 22%;
Cold Crushing Strength: 30MPa;
Refractoriness Under Load: 1640-1660;
Fe2o3: 1.0-1.4%;
Sio2: 94-96%;
|
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Low Thermal Conductivity, Permeability, Thermal Shock Resistance, Long Time Materials;
Refractoriness (℃): 1580< Refractoriness< 1770, 1000;
Shape: Plate, Plate;
Type: Calcium Silicate Boards;
Material: Calcium Silicate;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Bulk Density: 230;
Compressive Strength: 0.52-0.6MPa;
Thermal Conductivity: 0.05-0.062W/M.K;
Specification Temp: 1050/650;
Bending Strength: 0.3-0.45;
Sio2: 43%;
Cao: 44%;
|