| Specification |
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Permeability, Volume Stability;
Production Process: Extrusion;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Sio2: 89%~92%;
Bulk Density: 0.6g/cm3~1.2g/cm3;
Cold Crushing Strength: 2.5~5.0 MPa;
|
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Low Thermal Conductivity, Permeability, Thermal Shock Resistance, Long Time Materials;
Refractoriness (℃): 1580< Refractoriness< 1770, 1000ºC;
Shape: Plate, Plate;
Type: Calcium Silicate Boards;
Material: Calcium Silicate;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Bulk Density: 230;
Compressive Strength: 0.52-0.6MPa;
Thermal Conductivity: 0.05-0.062W/M.K;
Specification Temp: 1050/650;
Bending Strength: 0.3-0.45;
Sio2: 43%;
Cao: 44%;
|
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Low Thermal Conductivity, Permeability, Thermal Shock Resistance, Long Time Materials;
Refractoriness (℃): 1580< Refractoriness< 1770, 1000ºC;
Shape: Plate, Plate;
Type: Calcium Silicate Boards;
Material: Calcium Silicate;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Bulk Density: 230;
Compressive Strength: 0.52-0.6MPa;
Thermal Conductivity: 0.05-0.062W/M.K;
Specification Temp: 1050/650;
Bending Strength: 0.3-0.45;
Sio2: 43%;
Cao: 44%;
|
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Low Thermal Conductivity, Permeability, Thermal Shock Resistance, Long Time Materials;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate, Ceramic Fiber Blanket;
Usage: High Temperature Insulating Material;
Temprature Classification: 1050℃, 1350ºC;
Chemical Composition: Al2O3.Sio2;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Type: Heat-Resistant Material;
Temperature: 650c, 1000c, 1050c;
Certifiacte: ISO9001:2000;
|
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Low Thermal Conductivity, Permeability, Thermal Shock Resistance, Long Time Materials;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate, Plate;
Usage: High Temperature Insulating Material;
Temprature Classification: 1050℃, 1350ºC;
Chemical Composition: Al2O3.Sio2;
Manufacturing Technique: Static Autoclave Method;
Kind: Thermal Ceramic Material;
Type: Heat-Resistant Material;
Temperature: 650c, 1000c, 1050c;
Certifiacte: ISO9001:2000;
|