| Specification |
Sio2: 89%~92%;
Bulk Density: 0.6g/cm3~0.8g/cm3;
Cold Crushing Strength: 2.5MPa~5.0MPa;
Fe2o3: 0.6%;
|
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Low Thermal Conductivity, Thermal Shock Resistance, Volume Stability, Long Time Materials;
Production Process: Semi-Dry Pressing;
Refractoriness (℃): 1580< Refractoriness< 1770, 1770< Refractoriness< 2000;
Shape: Brick, Brick;
Type: Silica Brick, Refractory Material;
Material: Silica Sand;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 22%;
Cold Crushing Strength: 30MPa;
Refractoriness Under Load: 1640-1660;
Fe2o3: 1.0-1.4%;
Sio2: 94-96%;
|
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Low Thermal Conductivity, Thermal Shock Resistance, Volume Stability, Long Time Materials;
Production Process: Semi-Dry Pressing;
Refractoriness (℃): 1580< Refractoriness< 1770, 1770< Refractoriness< 2000;
Shape: Brick, Brick;
Type: Silica Brick, Refractory Material;
Material: Silica Sand;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 22%;
Cold Crushing Strength: 30MPa;
Refractoriness Under Load: 1640-1660;
Fe2o3: 1.0-1.4%;
Sio2: 94-96%;
|
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Low Thermal Conductivity, Permeability, Thermal Shock Resistance;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate, Board;
Usage: High Temperature Insulating Material;
Temprature Classification: 1050℃;
Manufacturing Technique: Stirring, Heating, Gelling, Forming, Drying;
Chemical Composition: Sio2+Cao;
Kind: Reinforcing Fiber;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Working Temp: 1000c;
Bulk Density: 250kg/M3;
Compressive Strength: 0.52MPa;
Thermal Conductivity: 0.050W/M.K;
The Max Temp: 1050c;
Link Shrinkage: 1.5%@1050*3hrs;
Bending Strength: 0.45MPa;
|
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Low Thermal Conductivity, Thermal Shock Resistance, Volume Stability, Long Time Materials;
Production Process: Semi-Dry Pressing;
Refractoriness (℃): 1580< Refractoriness< 1770, 1770< Refractoriness< 2000;
Shape: Brick, Brick;
Type: Silica Brick, Refractory Material;
Material: Silica Sand;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 22%;
Cold Crushing Strength: 30MPa;
Refractoriness Under Load: 1640-1660;
Fe2o3: 1.0-1.4%;
Sio2: 94-96%;
|