Specification |
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Al2O3: ≥90%;
Bulk Density: 1.4G/Cm3-1.7g/cm3;
Sio2: ≤0.5%;
Cold Crushing Strength: ≥9MPa;
|
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Roll, Ceramic Fiber Blanket;
Usage: High Temperature Insulating Material;
Temprature Classification: 1260℃, 1050℃, 1430;
Chemical Composition: Al2O3.Sio2;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Specification Temp: 1260/1360/1430;
Certifiacte: ISO9001, CE, etc;
Working Temperature: 1050-1350;
Bulk Density(g/cm3): 96-160;
Linear Shrinkage After Heating: -3;
Thermal Conductivity: 0.09-0.76;
Al2O3: 34-52;
Al2O3+Sio2: 96-99;
Tensile Strength: 0.05-0.06;
|
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Long Time Materials;
Production Process: Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770, 1770< Refractoriness< 2000;
Shape: Brick, Brick;
Type: Refractory Material;
Material: Alumina Block;
Al2O3: 48%~85%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Refractoriness: Sk35, Sk36, Sk37, Sk38, Sk40;
Apparent Porosity: 20-23%;
Bulk Density: 2.25-2.65g/cm3;
Refractoriness Under [email protected]: 1380-1550;
Thermal Linear Expansion@1000deg: 0.6%;
Fe2o3: 1.8-2.0%;
|
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Long Time Materials;
Production Process: Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770, 1770< Refractoriness< 2000;
Shape: Brick, Brick;
Type: Refractory Material;
Material: Alumina Block;
Al2O3: 48%~85%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Refractoriness: Sk35, Sk36, Sk37, Sk38, Sk40;
Apparent Porosity: 20-23%;
Bulk Density: 2.25-2.65g/cm3;
Refractoriness Under [email protected]: 1380-1550;
Thermal Linear Expansion@1000deg: 0.6%;
Fe2o3: 1.8-2.0%;
|
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity, Long Time Materials;
Production Process: Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770, 1580< Refractoriness< 1770;
Shape: Brick, Brick;
Type: Refractory Material;
Material: Mullite;
Bulk Density(g/cm3): 0.6g/cm3;
Al2O3: 40%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
|