Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Sio2: ≥48%;
Bulk Density: 400kg/M3~500kg/M3;
|
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Low Thermal Conductivity, Permeability, Thermal Shock Resistance;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate, Board;
Usage: High Temperature Insulating Material;
Temprature Classification: 1050℃;
Manufacturing Technique: Stirring, Heating, Gelling, Forming, Drying;
Chemical Composition: Sio2+Cao;
Kind: Reinforcing Fiber;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Working Temp: 1000c;
Bulk Density: 250kg/M3;
Compressive Strength: 0.52MPa;
Thermal Conductivity: 0.050W/M.K;
The Max Temp: 1050c;
Link Shrinkage: 1.5%@1050*3hrs;
Bending Strength: 0.45MPa;
|
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Low Thermal Conductivity, Permeability, Thermal Shock Resistance, Long Time Materials;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate, Plate;
Type: Calcium Silicate Boards;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Bulk Density: 230;
Compressive Strength: 0.52-0.6MPa;
Thermal Conductivity: 0.05-0.062W/M.K;
Specification Temp: 1050/650;
Bending Strength: 0.3-0.45;
Sio2: 43%;
Cao: 44%;
|
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Low Thermal Conductivity, Permeability, Thermal Shock Resistance;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate, Board;
Usage: High Temperature Insulating Material;
Temprature Classification: 1050℃;
Manufacturing Technique: Stirring, Heating, Gelling, Forming, Drying;
Chemical Composition: Sio2+Cao;
Kind: Reinforcing Fiber;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Working Temp: 1000c;
Bulk Density: 250kg/M3;
Compressive Strength: 0.52MPa;
Thermal Conductivity: 0.050W/M.K;
The Max Temp: 1050c;
Link Shrinkage: 1.5%@1050*3hrs;
Bending Strength: 0.45MPa;
|
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Low Thermal Conductivity, Permeability, Thermal Shock Resistance;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate, Board;
Usage: High Temperature Insulating Material;
Temprature Classification: 1050℃;
Manufacturing Technique: Stirring, Heating, Gelling, Forming, Drying;
Chemical Composition: Sio2+Cao;
Kind: Reinforcing Fiber;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Working Temp: 1000c;
Bulk Density: 250kg/M3;
Compressive Strength: 0.52MPa;
Thermal Conductivity: 0.050W/M.K;
The Max Temp: 1050c;
Link Shrinkage: 1.5%@1050*3hrs;
Bending Strength: 0.45MPa;
|