Specification |
Classification: Corundum;
Feature: Good Mechanical Strength, High-Temperature Resistant;
Production Process: Casting Method;
Refractoriness (℃): Refractoriness> 2000;
Shape: Brick;
Al2O3: ≥90%;
Bulk Density: ≥3.0g/cm3;
Apparent Porosity: ≤19%;
Cold Crushing Strength: ≥100MPa;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Calcined;
Refractoriness (℃): Refractoriness> 2000;
Shape: Fepa Size, Grain Size, Powder;
Advantage I: Low Calorific Value, High Efficiency;
Advantage II: High Purity, Good Self-Sharpening;
High Quality: Low Na2o High B.D.;
Advantage III: High Temperature and Thermal Stability;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Stirring Processing;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Powder;
Item: Refractory Castable;
Bulk Density: 2.2-2.7 g/cm3;
Color: Grey, White;
Application: Industrial Furnaces;
Advantage: High Temperature Resistant;
Service Tempera: 1200-1700 ºC;
Cold Crushing Strength: 40-80 MPa;
Chemical Analysis: Al2O3/Cao/Fe2o3;
Production Time: 15-30 Days;
Customized: Acceptable;
Testing Laboratory: Support;
Thermal Shock Resistance: Excellent;
Quality Assurance: Yes;
Performance: Excellent;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Powder;
Size: Customized;
|
Classification: Refractory Materials;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Production Process: Sintering Method;
Refractoriness (℃): Refractoriness<1580;
Shape: Plate;
Product Name: Alumina Ceramic Foam Filter;
Application: Aluminum Alloys and Others Nonferrous Metal Alloys;
Pore Density (Ppi): 10-40;
Operating Temperature: <1200 Celsius Degree;
Thickness: 12-25mm;
Porosity (%): 80-90;
Bending Strength (MPa): >0.6;
Compression Strength (MPa): >0.8;
Thermal Sgock Resistance (Times/1100): 6;
Color: White;
|