Specification |
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, High Melting Point, Thermal Shock Resistance;
Production Process: Sintering Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Brick;
Al2O3: Min60%;
Application: Anode Baking Furnace;
Brick: Andalusite Brick;
Refractory Material: Fireproof Material;
High Alumina Brick: Corundum Brick;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance;
Production Process: Sintering Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Brick;
Color: Black;
Application: Anode Baking Kiln;
Shelf Life Min: 6 Months;
Raw Material: Carbon;
|
Feature: Corrosion Resistance, Good Insulation Performance, Thermal Shock Resistance;
Production Process: Sintering Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Ring;
Color: White, Light Yellow;
Density: 2.1 g/cm3;
Working Temperature: 1300c;
Size: Customized;
Usage: Barbecue Grill, Burn Oven, Convection Oven, Gas Ov;
Keyword1: Refractory Welding Ceramic;
Keyword2: Cordierite Ceramic Ferrule Ring;
Thermal Expansion 1000 C: 6.5;
MOQ: 2 PCS;
|
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, Thermal Shock Resistance, Long Time Materials;
Production Process: Sintering Method;
Refractoriness (℃): 1580< Refractoriness< 1770, 1580< Refractoriness< 1770;
Shape: Brick, Block;
Type: Refractory Material;
Material: Alumina Block;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 18-20%;
Bulk Density: 2.75-3.1g/cm3;
Cold Crushing Strength: 70-90MPa;
Refractoriness Under Load: 1650-1700ºC;
Al2O3: 85-98.5%;
Fe2o3: 0.2-0.5%;
Sio2: 0.3-18%;
|