| Specification |
Material: Natural Silica Mine;
Content: >90%;
Usage: Grind;
Processing Type: Grinding;
Size: 2-4cm, 4-6cm, 6-8cm, 8-10cm, 10-12cm, 12-15cm;
Color: White;
Sio2: >=99.31%;
Density: >=2.66~2.68g/cm3;
Hardness: >=8;
Al2O3: <=0.36%;
Fe2o3: <=0.018;
Shape: Round;
Item: Silica Pebbles Used for Ceramic Ball Mill Grinding;
|
Material: Ceramics;
Content: >90%;
Usage: Machinery, Chemical, Grind, Refractory Material;
Processing Type: Isostatic Pressing Type and Rolling Type;
Size: 0.5-120mm;
Color: Brown;
Customized: Customized;
Ai2o3: 95%;
Sio2: 2.80%;
Fe2o3: 0.01%;
Roundness: 95%;
Rapid Wear Loss: Less Than or Equal to 0.7 G/Kg.H;
Colour: White;
Compression Strength: More Than or Equal to 2250 MPa;
Hardness: 9 Mohs;
Water Absorption: Less Than or Equal to 0.01%;
Equivalent Wear Loss: Less Than or Equal to 0.0008%;
HS: 69091200;
Bulk Density: 3.7g Per Cubic Meter;
Moulding Rolling: 0.5-20mm;
Isostatic Pressing: 25-90mm;
|
Material: Ceramics;
Content: >90%;
Usage: Machinery, Grinding Media;
Processing Type: Rolling Type;
Size: Small;
Color: White;
Customized: Non-Customized;
Shape: Round and Cylindrical;
Sample: Availabale;
Self Consumption: <0.3 Ppm/H;
Roundness: >/=0.98 (Xmin/Xmax);
Vickers Hardness: >1350;
Bulk Density: >/=3.7g/cm3;
Compressive: >2.0kn (Dia 2mm);
Density: >6.05g/cm3;
Model No.: Kingda-33;
Water Absorbation: <0.01%;
MOQ: 1 Kg;
Moh′s Hardness: >9;
Surface Smooth as a Mirror: Basic No Pollution for The Material;
Name of Chemical: Zirconia Ceramic Beads;
|
Material: Ceramics;
Content: >90%;
Usage: Machinery, Chemical, Grind, Refractory Material;
Processing Type: Isostatic Pressing Type and Rolling Type;
Size: 0.5-120mm;
Color: Brown;
Customized: Customized;
Ai2o3: 95%;
Sio2: 2.80%;
Fe2o3: 0.01%;
Roundness: 95%;
Rapid Wear Loss: Less Than or Equal to 0.7 G/Kg.H;
Colour: White;
Compression Strength: More Than or Equal to 2250 MPa;
Hardness: 9 Mohs;
Water Absorption: Less Than or Equal to 0.01%;
Equivalent Wear Loss: Less Than or Equal to 0.0008%;
HS: 69091200;
Bulk Density: 3.7g Per Cubic Meter;
Moulding Rolling: 0.5-20mm;
Isostatic Pressing: 25-90mm;
|
Material: Ceramics;
Content: >90%;
Usage: Machinery, Chemical, Grind, Refractory Material;
Processing Type: Isostatic Pressing Type and Rolling Type;
Size: 0.5-120mm;
Color: Brown;
Customized: Customized;
Ai2o3: 95%;
Sio2: 2.80%;
Fe2o3: 0.01%;
Roundness: 95%;
Rapid Wear Loss: Less Than or Equal to 0.7 G/Kg.H;
Colour: White;
Compression Strength: More Than or Equal to 2250 MPa;
Hardness: 9 Mohs;
Water Absorption: Less Than or Equal to 0.01%;
Equivalent Wear Loss: Less Than or Equal to 0.0008%;
HS: 69091200;
Bulk Density: 3.7g Per Cubic Meter;
Moulding Rolling: 0.5-20mm;
Isostatic Pressing: 25-90mm;
|