Specification |
Color: Transparent;
Heat Resistance: High Temperature;
Waterproof: Waterproof;
Application: Paper, Plastic, Metal, Rubber, Wood, Leather, Textile, Glass, Ceramic;
Adhesive: Acrylic Acid;
Base Material: Crepe Paper;
Type: Double Sided Tape;
Carrier: Self Adhesive Acrylic Foam;
Liner: Red Green and Blue Liner;
Total Thickness: 0.25mm-1.5mm;
Holding Power: 24 Hrs;
Density Temperature Resistance: -20degree Centigrade-150 Degree Centigrade;
|
Color: Green;
Heat Resistance: High Temperature;
Waterproof: Waterproof;
Application: Paper, Plastic, Rubber, Wood, Leather, Textile, Glass, Ceramic;
Adhesive: Silica Gel;
Base Material: Pet;
Type: Pressure-Sensitive Tape;
180°peel Strength[N/Inch]: 8;
Long-Term Temperature [ºC]: 180;
Short-Term Temperature[ºC]: 200;
Sample: Freely Provided;
Tensile Strength[N/Inch]: 135;
Elongation at Break[%]: 70;
|
Color: Green;
Heat Resistance: High Temperature;
Waterproof: Waterproof;
Application: Paper, Plastic, Rubber, Wood, Leather, Textile, Glass, Ceramic;
Adhesive: Silica Gel;
Base Material: Pet;
Type: Pressure-Sensitive Tape;
180°peel Strength[N/Inch]: 8;
Long-Term Temperature [ºC]: 180;
Short-Term Temperature[ºC]: 200;
Sample: Freely Provided;
Tensile Strength[N/Inch]: 150;
Elongation at Break[%]: 70;
|
Color: Gold;
Heat Resistance: High Temperature;
Waterproof: Waterproof;
Application: Paper, Plastic, Rubber, Wood, Leather, Textile, Glass, Ceramic;
Adhesive: Silica Gel;
Base Material: Pet;
Type: Pressure-Sensitive Tape;
180°peel Strength[N/Inch]: 5;
Long-Term Temperature [ºC]: 260;
Short-Term Temperature[ºC]: 280;
Sample: Freely Provided;
Tensile Strength[Kg/25mm]: 10;
Elongation at Break[%]: 5;
|
Color: Gold;
Heat Resistance: High Temperature;
Waterproof: Waterproof;
Application: Paper, Plastic, Rubber, Wood, Leather, Textile, Glass, Ceramic;
Adhesive: Silica Gel;
Base Material: Pet;
Type: Pressure-Sensitive Tape;
180°peel Strength[N/Inch]: 6;
Long-Term Temperature [ºC]: 260;
Short-Term Temperature[ºC]: 280;
Sample: Freely Provided;
Tensile Strength[Kg/25mm]: 9;
Elongation at Break[%]: 45;
|