Specification |
CAS No.: None;
Formula: None;
EINECS: None;
Molecular Principal Chain: Na;
Color: Light Yellow, Beige;
Name: Pw100 PLA Water Washable Resin;
Net Weight: 0.5kg/1kg;
Gross Weight: 0.75kg/1.5kg;
Density (G/Cm³): 1.09-1.10;
Viscosity (Mpas): 90-150;
Flexural Strength (MPa): 34-47;
Izod Impact Strength (J/M): 950-1050;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 55-95;
Density,g/cm3: 1.19-1.22;
100% Modulus,MPa: 4-26;
300% Modulus,MPa: 8-28;
Tensile Strength,MPa: 30-50;
Tear Strength,MPa: 100-240;
Procesing Temperature,°c: 165-180;
|
CAS No.: 9009-54-5;
EINECS: 210-898-8;
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 72-95;
Density,g/cm3: 1.19-1.20;
100% Modulus,MPa: 3-11;
300% Modulus,MPa: 8-26;
Tensile Strength,MPa: 32-50;
Tear Strength,MPa: 90-160;
DIN Abrasion Loss,mm³: 30-35;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 79-89;
Density,g/cm3: 1.2-121;
Tensile Strength,MPa: 24-30;
Tear Strength,MPa: 75-90;
Elongation at Break,%: 600-800;
Tg ,ºC: -18~-36;
|
CAS No.: 9009-54-5;
EINECS: 210-898-8;
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 79-89;
Density,g/cm3: 1.2-121;
Tensile Strength,MPa: 24-30;
Tear Strength,MPa: 75-90;
Elongation at Break,%: 600-800;
Tg ,ºC: -18~-36;
|