Specification |
Usage: Thermal Insulation Coatings, High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber, High Purity Ceramic Fiber;
Chemical Composition: Al2O3.Sio2, Al2O3;
Thickness: 6~50mm;
Fiber Diameter: 3.5um;
Quality Certificate: ISO9001-2008 ISO14001-2004;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1260℃, 1050℃, 1350ºC;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Feature: Long Time Materials;
Type: Heat-Resistant Material;
Temperature: 1260c, 1350c, 1430c;
Certifiacte: ISO9001:2000;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1050℃;
Chemical Composition:: Sio2+Cao;
Shape: Board;
Manufacturing Technique: Stirring, Heating, Gelling, Forming, Drying;
Kind: Reinforcing Fiber;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Working Temp: 1000c;
Bulk Density: 250kg/M3;
Compressive Strength: 0.52MPa;
Thermal Conductivity: 0.050W/M.K;
The Max Temp: 1050c;
Link Shrinkage: 1.5%@1050*3hrs;
Bending Strength: 0.45MPa;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Mat;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Module;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Classification Temperature: 1260c;
Certifiacte: ISO9001:2000;
Bulk Density: 160-220 Kg/Cm3;
Al2O3: 44%;
Sio2: 52%;
Fe2o3+TiO2: 1.0%;
Thermal Conductivity@400c: 0.09W/M.K;
Thermal Conductivity@500c: 0.119W/M.K;
Thermal Conductivity@600c: 0.152W/M.K;
Linear Shrinkage After Heating: 2.5%@1000c*24h;
|