| Specification |
Usage: High Temperature Insulating Material;
Temprature Classification: 1260℃;
Chemical Composition:: Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Textile;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Density: 463.9kg/M3;
Thickness: 2mm;
Standard: Reach GB8624A(Ai);
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Plate;
Manufacturing Technique: vacuum Formed;
Kind: High Purity Ceramic Fiber;
Length: 1200mm;
Width: 1000mm;
Min Thickness: 3mm;
Max Thickness: 100mm;
Density: 220kg/M3 -350kg/M3;
Color: White;
Shapes: Can Be Cut to Any Shapes;
Loss of Ignition, Loi, %: <8%;
Types: Inroganic Type and Organic Type;
Shrinkage, %,: <3;
Compressive Strength,: >0.2;
Thermal Conductivity, W/M•K: 0.03-0.18;
Smell: Inorganic Type Has No Smell;
Refractory Grade: Non-Inflammable;
Application: Oven, Furnace, Boiler Heat Insulation Liner;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Different Shapes;
Manufacturing Technique: Vacuum Formed;
Kind: High Purity Ceramic Fiber;
Shapes: Can Be Made Different Shapes;
Density: 280kg/M3-450kg/M3;
Color: White;
Organic Type: with Smell;
Inorganic Type: Without Smell;
Application: Boiler, Furnace, Stove etc;
Loss of Ignition, Loi, %: <8;
Permanent Linear Shrinkage, %, 24 Hours: <3;
Compressive Strength: >0.2;
Thermal Conductivity, W/M•K: 0.06-0.18;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1200, 1300ºC;
Chemical Composition:: Calcium, Magnesium, Silicate Chemistry;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: Bio-Soluble Fiber;
Standard Densities: 96, 128 Kg/M3;
Standard Thickness: 1", 2";
Standard Width: 24" and 48";
Thermal Shock Resistance: Good;
Features: Light Weight, Low Heat Storage, etc.;
Application: Furnace/Kiln/Heater Lining, Mould, Pipe Wrap, etc.;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1200, 1300ºC;
Chemical Composition:: Calcium, Magnesium, Silicate Chemistry;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: Bio-Soluble Fiber;
Standard Densities: 96, 128 Kg/M3;
Standard Thickness: 1", 2";
Standard Width: 24" and 48";
Thermal Shock Resistance: Good;
Features: Light Weight, Low Heat Storage, etc.;
Application: Furnace/Kiln/Heater Lining, Mould, Pipe Wrap, etc.;
|