Specification |
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: GB, ASTM;
Purity: >99.99%;
Alloy: Alloy;
Type: In625;
Powder: Powder;
Appearance: Spherical;
Color: Grey;
MOQ: 1kg;
Material: Nickel Alloy Powder;
Technology: Prep, Gas Atomization;
Feature: Corroison Resistance;
Size Range: Customized;
|
Application: Industrial;
Standard: ASTM;
Purity: 58%;
Alloy: Alloy;
Type: Nickel Wire;
Powder: Not Powder;
Surface: Bright;
Chemistry Composition: Ni Cr Mo Fe W Co;
Melting Point: 1325-1370 ºC;
Density: 8.89g/cm3;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Alloy: Alloy;
Type: Nickel Bar;
Powder: Not Powder;
Density: 8.47;
Elongation: 2~5;
Sample: Free;
Technology: Cold Drawing;
Melting Range: 1354-1413c;
Tensile Strength: 1170-1520MPa;
Yield Strength: 1035-1450MPa;
Surface: Bright/Acid White/Oxidation;
Condition: Soft Annealed/Hard;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI, ISO 9001;
Purity: 63%;
Alloy: Non-alloy;
Type: Nickel Bar;
Powder: Not Powder;
Melting Point: 1300~1390;
Surface: Bright/Oxidation;
Elongation (A5%): 35;
Tensile Strength: 480MPa;
Yield Strength: 170MPa;
Hb: Min 331;
Density: 8.9g/cm3;
Shape: Wrie, Pipe, Bar, Strip, Plate;
Technique: Cold Treatment;
Manufacturing Process: Solution Treatment;
Size: 10~200mm;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI, ISO 9001;
Purity: >98%;
Alloy: Alloy;
Type: CuNi Wire;
Powder: Not Powder;
Technique: Cold Drawing;
Treatment: Hydrogen Annealing;
Surface: Bright;
Condition: Soft Annealed;
Usages: Welding Tool;
Resistivity: 0.5;
Density: 8.9 g/cm3;
TCR X10-6 / 0c (20~600 0c): <-6;
Emf Vs Cu (μV/ 0c) (0~100 0c): -43;
Melting Point: 1200c;
|