Specification |
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Hookend;
Material: High Chrome Aluminium;
Condizioni Stabili (ºC): 1300;
Cicli Termici (ºC): 1460;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Cement;
Name: Red Fire Clay Brick;
Density (g/cm3): 2.05-2.75;
Standard Size (mm): 230*114*65mm;
Permanent Linear Change % 1500cx2h: -0.5%~+0.1%;
Refractoriness: 1740;
Cold Crushing Strength MPa: 20;
Apparent Porosity: 24%;
0.2 MPa Refractoriness Under: 1350c;
Color: Red Fire Brick;
Application: Fire Clay Brick for Industrial Furnaces;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Heat-Resistant Material;
Shape: Pipe;
Material: Alumina Block;
Color: Ivory,White;
Features: High Temperature Resistant;
Size: Customize;
Usage: Furnace,Kiln;
Diameter: Customize;
Length: Customize;
Delivery Time: 3-30 Days;
Density: 3.6-3.9g/cm3;
Temperature: 1600c 1800c;
Brand: Mission;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Ring;
Material: Alumina Block;
Color: Ivory, White;
Package: Wooden Box;
Delivery Time: 3-30 Days;
Density: 3.6-3.9g/cm3;
Features: High Wear Resistant;
Diameter: Customize;
Thickness: Customize;
Brand: Mission;
Max Temperature: 1600c 1800c;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Square, Circular, Triangular, etc;
Material: Mullite, Cordierite, High Alumina, etc;
Size: 50*50, 40*40, 65*65, 50*75, etc;
Hole: Square, Circular, Triangular, Hexagonal, etc;
Holes: 100cpsi, 200cpsi, 300cpsi, etc;
|