Specification |
Refractoriness (℃): Greater Than 1100 Degree;
Feature: Instant Materials;
Type: Heat-Resistant Material;
Shape: Needle/Fiber;
Material: Stainless Steel;
Tensile Strength: 650MPa;
Erosion in The H2,at 454,Mil/Yr: 21.9;
Carbon Content of The Alloy After Solid: Lower Than 0.30%;
Max Working Temp. in The So2: 1100 Degree;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Product Name: Alumina Ceramic Filter Plate;
Model No.: Sf-Acf;
Pore Density(Ppi): 10-40;
Porosity(%): 80-90;
Operating Temperature: <1100celsius;
Bending Strength(MPa): >1.0;
Compression Strength(MPa): >0.8;
Thermal Sgock Resistance(Times/1100): 6;
Color: White;
Filter Shape: Square/Round or Custom;
Size: According to Clients Requirements;
Features 1: High Strength, No Slag, Good Thermal Shock Resista;
Features 2: High Porosity, Excellent Filtration Result;
Sizes Complete: 7 Inch to 26 Inch, 10ppi to 70ppi.;
Sealing Gasket: Fiber Paper, Fiber Cotton and Expandable Cotton;
|
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Plate;
Material: Alumina Cement;
Product Name: Alumina Ceramic Filter Plate;
Pore Density(Ppi): 10-40;
Porosity(%): 80-90;
Operating Temperature: <1100celsius;
Bending Strength(MPa): >1.0;
Compression Strength(MPa): >0.8;
Thermal Sgock Resistance(Times/1100): 6;
Filter Shape: Square/Round or Custom;
Size: According to Clients Requirements;
Features 1: High Strength, No Slag, Good Thermal Shock Resista;
Features 2: High Porosity, Excellent Filtration Result;
Sizes Complete: 7 Inch to 26 Inch, 10ppi to 70ppi.;
Sealing Gasket: Fiber Paper, Fiber Cotton and Expandable Cotton;
|
Refractoriness (℃): 32 34;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Raw material: alumina, other materials;
application: anchorage;
Lead time: 40 days to 60 days according to the market;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magnesia-Hecynite;
Application Area: transitional Zone in Rotary Kiln;
Size: Customer Made;
Bulk Density: 2.65~2.7g/cm3;
Apparent Porosity: 20 %;
TSR - in water at 1100ºC: 10-15 Cycle;
Refractoriness Under Load: 1650;
CCS MPa: 80-100;
|