Specification |
Material: PTFE;
Kind: Plastic Bar;
Water Absorption: <0.01%;
Contraction Percentage: <0.4%;
Tensile Strength: 30~40MPa;
Length: 100mm ~ 3000mm;
Sample: Avilable;
Temp: -180 ~ + 260;
Color: White;
Fillers: Fiberglass, Carbon, Graphite, Bronze;
Crack Elongation: >150%;
Density: 2.1 ~ 2.3 g/cm3;
Diameter: 3mm~300mm;
|
Material: Peek;
Kind: Special Engineering Plastics;
Water Absorption: 0.5;
Contraction Percentage: <0.4%;
Tensile Strength: 81~130MPa;
Use: Aircraft Engine Parts;
Color: Brown;Black;
Attributes: Self-Lubricating; Easy to Process;
Processing Methods: Mold Opening Injection, Profile Machining;
|
Material: PTFE;
Kind: Plastic Bar;
Water Absorption: 0;
Contraction Percentage: 0;
Tensile Strength: 0;
Packing: 200PCS/CTN;
Materials: PTFE;
Color: White;
Composite: Neodymium Magnet;
Processing Service: Bending, Welding, Decoiling, Cutting, Punching, Mo;
Size: Customized Size;
Sample: Free;
Product Name: Magnetic Stirrer Bar;
|
Material: PVC;
Kind: Hard Plastic Rods;
Water Absorption: <0.01%;
Contraction Percentage: <0.4%;
Tensile Strength: 41~50MPa;
Sizes: 10mm-300mm;
Stardard Color: Dark Grey(Ral7011),Balck White Red;
|
Material: PTFE;
Kind: Color Plastic;
Water Absorption: <0.01%;
Contraction Percentage: <0.4%;
Tensile Strength: 25-45MPa;
Density: 2.1--2.2 G/M3;
Elongation at Break: 200-350%;
Compression Strength: 24MPa;
Working Temp.: -180~260ºC;
Melting Point: 330ºC;
Produce Max.Temp.: 390ºC;
Fire Resistance: V-0;
Bittle Point Temperature: -268ºC;
Dielectric Strength: >1400kv/mm;
Dielectric Constant: 2.1;
|