| Specification |
CAS No.: 9010-98-4;
Formula: C4h5cl;
EINECS: 618-463-8;
Bonding Function: Shoes Making Glue;
Morphology: Solvent;
Application: Automobile, Construction, Footwear & Leather, Fiber & Garment, Packing, Shoes Repairing;
Material: Chloroprene Rubber;
Classification: Room Curing;
Main Agent Composition: Natural Polymer;
Characteristic: Weatherability;
Promoter Composition: Solvent;
Composition: Organic Material;
Color: Yellow;
Appearance: Slight Yellow Viscous Liquid;
Solid Content: 20% - 24%.;
Viscosity(25 Degrees Celsius): 2000 - 4000cps.;
Density: 0.92kg/L.;
Tack Time: 60 Minutes;
Suitable Material: Rubber, Leather, Cloth, Paper, EVA etc.;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, High Shear Strength, Fast Cure;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Density: 1.20±0.05 Kg/L;
Cure Mechanism: Moisture-Curing;
Non-Sag Properties: Good;
Shore a Hardness: ~ 60;
Shear Strength: ≥ 5 N/mm^2;
Tensile Strength: ≥ 8 N/mm^2;
Elongation at Break: ≥ 400%;
Tear Strength: ≥ 10 N/mm;
Tack-Free Time (23 ºC , 50% Rh): 20~40 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3.5 mm/24hrs;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, High Shear Strength, Fast Cure;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Density: 1.20±0.05 Kg/L;
Cure Mechanism: Moisture-Curing;
Non-Sag Properties: Good;
Shore a Hardness: ~ 60;
Shear Strength: ≥ 5 N/mm^2;
Tensile Strength: ≥ 8 N/mm^2;
Elongation at Break: ≥ 400%;
Tear Strength: ≥ 10 N/mm;
Tack-Free Time (23 ºC , 50% Rh): 20~40 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3.5 mm/24hrs;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, High Shear Strength, Fast Cure;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Density: 1.20±0.05 Kg/L;
Cure Mechanism: Moisture-Curing;
Non-Sag Properties: Good;
Shore a Hardness: ~ 60;
Shear Strength: ≥ 5 N/mm^2;
Tensile Strength: ≥ 8 N/mm^2;
Elongation at Break: ≥ 400%;
Tear Strength: ≥ 10 N/mm;
Tack-Free Time (23 ºC , 50% Rh): 20~40 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3.5 mm/24hrs;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, High Shear Strength, Fast Cure;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Density: 1.20±0.05 Kg/L;
Cure Mechanism: Moisture-Curing;
Non-Sag Properties: Good;
Shore a Hardness: ~ 60;
Shear Strength: ≥ 5 N/mm^2;
Tensile Strength: ≥ 8 N/mm^2;
Elongation at Break: ≥ 400%;
Tear Strength: ≥ 10 N/mm;
Tack-Free Time (23 ºC , 50% Rh): 20~40 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3.5 mm/24hrs;
|