Specification |
Refractoriness (℃): Refractoriness> 2000;
Feature: Long Time Materials;
Type: Abrasivea, Abrasive Blasting, Polishing,Refractory;
Shape: Fineness / Grit / Powder/ Grain;
Material: Brown Fused Alumina;
Chemical Al2O3: Min: 95%, Typical Value 95.3%;
More Applications: Abrasive, Blasting, Grinding, Polishing;
Advantage: Manufacturer, Tilting Furnace, Barmac, Twin Roll;
Other Name: Brown Corundum, Electro Corundum, Corundum;
Calcined: Electric Arc Furnace, Byer Chemical;
Grit 3: 0-100 Mesh, 0-200 Mesh, 0-325 Mesh;
Grit 2: 60#, 70#, 80#, 90#, 100#, 120#, 150#, 180#, 220#;
Grit 1: 12#, 14#, 16#, 20#, 24#, 30#, 36#, 40#, 46#, 54#,;
|
Refractoriness (℃): 1380;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Silicon Carbide (SiC);
colour: Dark-gray;
model number: SISIC;
SiC Content (%): 83.66%;
Density: under 3.02 g/cm3;
Open Porosity: <0.1%;
Bending strength: 250MPa/280MPa;
Modulus of Elastictiy: 330Gpa/300Gpa;
Thermal Conductivity: 45W/m.K(1200 Celsius);
Coefficiant of Thermal Expansion: 4.5K-1*10-6;
Moh"s Hardness: 9.15;
Vickers Hardness HV: 20Gpa;
Acid Alkaline-proof: Excellent;
Length: Customer's Required;
thickness: Customer's Required;
width: Customer's Required;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magnesia-Hecynite;
Application Area: Sintering Zone in Rotary Kiln;
Size: Customer Made;
Bulk Density: 2.9-2.95g/cm3;
Apparent Porosity: 17%;
Tsr 950ºC: 100 Cycle;
Rul: 1650-1700ºC;
CCS MPa: 60;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Instant Materials;
Type: Refractory Material;
Shape: Brick;
Material: Ceramic;
Types: 528-018;
Bulk Density: 1.7g;
Packing: Carton Box;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Instant Materials;
Type: Refractory Material;
Shape: Brick;
Material: Ceramic;
Types: 528-018;
Bulk Density: 1.7g;
|