Specification |
Type: PTFE Conveyor Belt;
Material: PTFE;
Inside Material: Fabric;
Feature: Oil-Resistant, Acid And Alkali Resistant, Tear-Resistant, Heat-Resistant, Cold-Resistant, Wear-Resistant;
Tensile Strength: 410 Lbs/Inch;
Color: Brown;
Base Fabric and Weave: Fiberglass/Satin Weave;
Temperature Resistance: -101 ºC to 315 ºC;
UV Resistance: 1000 Hrs; No Change in Tensile;
Thickness: 0.7mm;
Mullen Burst: 650 Psi;
Flame Resistance: Char Length 1 Inch Max;
Craft: Impregnating;
Chemical Reaction: Acid and Alkali Resistance;
MOQ: 100 M2;
Standard: Food Grade;
Friction Coefficient: 0.05;
Sample: Free Sample and Shipping;
Glass Fiber Grade: E-Glass;
Width: 400 - 1000 mm;
|
Type: EP250;
Material: Rubber;
Inside Material: Fabric;
Feature: Oil-Resistant, Acid And Alkali Resistant, Tear-Resistant, Heat-Resistant, Cold-Resistant;
Tensile Strength: Strong;
Tensile Strength of Covering Adhesive: 12MPa;
Width: 800mm;
Fabric Ply/Number of Plies: 4;
Top Cover Thickness: 6mm;
Bottom Cover Thickness: 2mm;
Color: Black;
|
Type: EP250;
Material: Rubber;
Inside Material: Fabric;
Feature: Oil-Resistant, Acid And Alkali Resistant, Tear-Resistant, Heat-Resistant, Cold-Resistant;
Tensile Strength: Strong;
Tensile Strength of Covering Adhesive: 12MPa;
Width: 800mm;
Fabric Ply/Number of Plies: 4;
Top Cover Thickness: 6mm;
Bottom Cover Thickness: 2mm;
Color: Black;
|
Type: EP250;
Material: Rubber;
Inside Material: Fabric;
Feature: Oil-Resistant, Acid And Alkali Resistant, Tear-Resistant, Heat-Resistant, Cold-Resistant;
Tensile Strength: Strong;
Tensile Strength of Covering Adhesive: 12MPa;
Width: 800mm;
Fabric Ply/Number of Plies: 4;
Top Cover Thickness: 6mm;
Bottom Cover Thickness: 2mm;
Color: Black;
|
Type: EP250;
Material: Rubber;
Inside Material: Fabric;
Feature: Oil-Resistant, Acid And Alkali Resistant, Tear-Resistant, Heat-Resistant, Cold-Resistant;
Tensile Strength: Strong;
Tensile Strength of Covering Adhesive: 12MPa;
Width: 800mm;
Fabric Ply/Number of Plies: 4;
Top Cover Thickness: 6mm;
Bottom Cover Thickness: 2mm;
Color: Black;
|