Specification |
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials, Refractory Materials;
Type: Refractory Material;
Shape: Brick;
Material: Spinel Brick;
MGO (%)>: 85%-90%;
Al2O3: 3%-6%;
Fe2o3: 3%-6%;
Sio2: 1%;
B.D. (g/cm3)>: 2.95g/cm3-3.05g/cm3;
a.P. (%)<: 17%;
C.C.S MPa>: 50MPa;
0.2MPa Refractoriness Under Load>: 1700c;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials, Hot Sale;
Type: Refractory Material;
Shape: Brick;
Material: Silicon Carbide (SiC);
Product Name: Silica Bricks;
Processing Service: Bending, Welding, Punching, DEC;
Refractoriness °c: 1790;
Refractoriness Under Load T1,°c: 1650;
Apparent Porosity %: 22-24;
True Density g/cm3: 2.33;
Cold Crushing Strength(MPa): ≥24.5;
Application: Metallurgy;
Standard Size: 230X114X65;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials, Hot Sale;
Type: Refractory Material;
Shape: Brick;
Material: Silicon Carbide (SiC);
Product Name: Silica Bricks;
Processing Service: Bending, Welding, Punching, DEC;
Refractoriness °c: 1790;
Refractoriness Under Load T1,°c: 1650;
Apparent Porosity %: 22-24;
True Density g/cm3: 2.33;
Cold Crushing Strength(MPa): ≥24.5;
Application: Metallurgy;
Standard Size: 230X114X65;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials, Hot Sale;
Type: Refractory Material;
Shape: Brick;
Material: Silicon Carbide (SiC);
Product Name: Silica Bricks;
Processing Service: Bending, Welding, Punching, DEC;
Refractoriness °c: 1790;
Refractoriness Under Load T1,°c: 1650;
Apparent Porosity %: 22-24;
True Density g/cm3: 2.33;
Cold Crushing Strength(MPa): ≥24.5;
Application: Metallurgy;
Standard Size: 230X114X65;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials, Hot Sale;
Type: Refractory Material;
Shape: Brick;
Material: Silicon Carbide (SiC);
Product Name: Silica Bricks;
Processing Service: Bending, Welding, Punching, DEC;
Refractoriness °c: 1790;
Refractoriness Under Load T1,°c: 1650;
Apparent Porosity %: 22-24;
True Density g/cm3: 2.33;
Cold Crushing Strength(MPa): ≥24.5;
Application: Metallurgy;
Standard Size: 230X114X65;
|