| Specification |
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magnesium;
MGO: 52%-77%;
Cao: 13%-42%;
Sio2: 1.2%-1.3%;
Fe2o3: <0.7%;
Bulk Density: >3.0g/cm3;
Apparent Porosity: <8%;
|
Material: Zirconia-Corundum, Zro2;
Refractoriness (℃): 1580< Refractoriness< 1770, 1580< Refractoriness< 1770;
Shape: Block, Block;
Usage: Aerospace, Environmental Protection Equipment, Glass Manufacturing, Industrial Kilns, Steel Smelting;
Feature: Long Time Materials;
Type: Refractory Material;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 1.3-2.0%;
Bulk Density: 3.4-4.0g/cm3;
Cold Crushing Strength: 350MPa;
Thermal Linear Expansion(%): 0.8;
Zro2: 32-40%;
Na2o: 1.3-1.5%;
Sio2: 13-15.5%;
|
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity, Long Time Materials;
Production Process: Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770, 1580< Refractoriness< 1770;
Shape: Brick, Brick;
Type: Refractory Material;
Material: Alumina Block;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Bulk Density: 0.6-1.25;
Cold Crushing Strength: 1.0-10MPa;
Thermal Conductivity: 0.17-0.51;
|
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Long Time Materials, Instant Materials;
Refractoriness (℃): 1580< Refractoriness< 1770, 1770< Refractoriness< 2000;
Shape: Powder, Powder;
Type: Refractory Material;
Material: Castable;
Al2O3: 30-90;
Sio2: 15-48;
Size: Customizable;
Application Limit Temp: 1000-1700;
|
Classification: Clay, Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Long Time Materials;
Production Process: Extrusion Method, Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770, 1580< Refractoriness< 1770;
Shape: Brick, Brick;
Type: Refractory Material;
Material: Alumina Block;
Al2O3: 35%~45%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Refractoriness: Sk32-34;
Apparent Porosity: 13-26%;
Bulk Density: 2.25-2.65g/cm3;
Refractoriness Under [email protected]: 1250-1500;
Thermal Linear Expansion@1000deg: 0.6%;
Fe2o3: 1.8-3.0%;
|