Specification |
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials, Refractory Materials;
Type: Heat-Resistant Material;
Shape: Brick;
Material: Magnesia Chrome;
Brand: Hitech;
MGO: 58%-73%;
Apparent Porosity: 17%-18%;
Cold Crushing Sternth: 40MPa-45MPa;
Cr2o3: 16%;
|
Refractoriness (℃): 1380;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Pipe;
Material: Silicon Carbide (SiC);
Delivery Time: 25-30 Days;
Raw Material: Toner, Silicon Powder;
Application: Industrial Ceramic,Refractory,Industrial Furnaces;
Size: as Customer Need;
Usage: Anti- Strong Acid and Alkali;
Density: More Than 3.02 g/cm3;
Thermal Conductivity: 45 (1200 Celsius);
Moh's Hardness: 9.15;
Vickers Hardness Hv: 20 Gpa;
Open porosity: Less than 0.1%;
Acid alkaline proof: Excellent;
|
Refractoriness (℃): 1380;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Pipe;
Material: Silicon Carbide (SiC);
Delivery Time: 25-30 Days;
Raw Material: Toner, Silicon Powder;
Application: Industrial Ceramic,Refractory,Industrial Furnaces;
Size: as Customer Need;
Usage: Anti- Strong Acid and Alkali;
Density: More Than 3.02 g/cm3;
Thermal Conductivity: 45 (1200 Celsius);
Moh's Hardness: 9.15;
Vickers Hardness Hv: 20 Gpa;
Open porosity: Less than 0.1%;
Acid alkaline proof: Excellent;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Plate;
Product Name: Honeycomb Ceramic Filter;
Application: Iron Casting;
Bulk Density (G/Cmj): 0.6-1.0;
Compressive Strength (MPa): >15;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Grain;
Material: Al2O3 & Sio2;
Available Sizes: 0-1mm,1-3mm,3-5mm,5-8mm,8-12mm etc,or Customized;
Working Temperature: up to 1050ºC;
Applications: Castables,Agriculture,Water Filtration,Buildings;
Product Feature: 100% Environmentally Friendly;
|