Specification |
Type: Refractory Material;
Sio2: 95%-96%;
Fe2o3: 0.5%;
Al2O3: 3%;
Bulk Density: 1.8g/cm3;
Refractoriness: 1710c-1730c;
Apparent Porosity: 22%;
Cold Crushing Strength: 29MPa-35MPa;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials, High Temperature Resistance;
Type: Refractory Material;
Shape: Brick;
Material: Magsite;
Product Name: Refractory Magnesia Brick;
Size of Basic Refractory: 230*114*65mm or Special S;
Refractoriness: Super-Class (Refractoriness> 2000;
Apparent Porosity: Max 16%;
Applications: Iron Steel Furnace,Glass Furnace,Ceme;
Advantage: High Refractoriness;
Cold Crushing Strength: Min 60 MPa;
Reheating Linear Change(1650 °c,2h): 0~-0.4;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials, High Temperature Resistance;
Type: Refractory Material;
Shape: Brick;
Material: Magsite;
Product Name: Refractory Magnesia Brick;
Size of Basic Refractory: 230*114*65mm or Special S;
Refractoriness: Super-Class (Refractoriness> 2000;
Apparent Porosity: Max 16%;
Applications: Iron Steel Furnace,Glass Furnace,Ceme;
Advantage: High Refractoriness;
Cold Crushing Strength: Min 60 MPa;
Reheating Linear Change(1650 °c,2h): 0~-0.4;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials;
Type: Heat-Resistant Material;
Shape: Pipe;
Material: Alumina Block;
Item: Alumina Ceramic Elbow Pipe Linings;
Alumina Content: 92% & 95%;
Density: 3.6~3.7g/Cc;
Compressive Strength: 850~1000MPa;
Size: Available and Customized Size;
Applied Equipment: Chute, Hopper, Silo, Bunker, Funnel, Pipe, Cyclone;
Application Industry: Cement, Coal, Mining, Steel, Thermal Power, etc.;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials, High Temperature Resistance;
Type: Refractory Material;
Shape: Brick;
Material: Magsite;
Product Name: Refractory Magnesia Brick;
Size of Basic Refractory: 230*114*65mm or Special S;
Refractoriness: Super-Class (Refractoriness> 2000;
Apparent Porosity: Max 16%;
Applications: Iron Steel Furnace,Glass Furnace,Ceme;
Advantage: High Refractoriness;
Cold Crushing Strength: Min 60 MPa;
Reheating Linear Change(1650 °c,2h): 0~-0.4;
|