Specification |
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Heat-Resistant Material;
Shape: Powder;
Material: Castable;
MGO ≥: 83;
Cao: 5.6-6.9;
Fe2o3: 4.0-5.5;
Granularity Composition (mm): 60;
Limit of Application Temperatureoc: 1750;
|
Refractoriness (℃): 1260c-1430c-1600c;
Feature: Long Time Materials;
Type: Heat-Resistant Material;
Shape: Block;
Material: Aluminate Silicate;
Temperature: 1260c, 1350c, 1430c;
Density: 180-220kg/M3;
Tensile Strength: 0.04 MPa;
Permanent Linear Change in Heating %: Belowe -3;
Al2O3: 46-54%;
Al2O3+Sio2: 99%;
Zro2: 1430c: 15-17%;
Fe2o3: Below 0.2%;
Na2o+K2o: Below 0.2%;
MOQ: 1ton;
Color: White;
Package: with Pallets;
Application: Thermal Insulation,Furnance,Furnance Lining;
Industry: Petrochemical,Metallurgical,Ceramics,Glass;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Silica Sand;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 22%;
Cold Crushing Strength: 30MPa;
Refractoriness Under Load: 1640-1660;
Fe2o3: 1.0-1.4%;
Sio2: 94-96%;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Al2O3: 48%~85%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Refractoriness: Sk35,Sk36,Sk37,Sk38,Sk40;
Apparent Porosity: 20-23%;
Bulk Density: 2.25-2.65g/cm3;
Refractoriness Under [email protected]: 1380-1550;
Thermal Linear Expansion@1000deg: 0.6%;
Fe2o3: 1.8-2.0%;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magnesia-Hecynite;
Application Area: Sintering Zone in Rotary Kiln;
Size: Customer Made;
Bulk Density: 2.9-3.0g/cm3;
Apparent Porosity: 17;
Tsr 950ºC: 100 Cycle;
Rul: 1650-1700ºC;
CCS MPa: 60;
|