Specification |
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magnesia Chrome;
Keywords: Magnesia Chrome Brick;
Application: Isa Furnace;
MGO: 70;
Cr2o3: 16;
Sio2%: 1.5%;
Bulk Density: >3.15g/cm3;
a.P. (%)<: 17%;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Powder;
Material: Castable;
Al2O3: 75%;
Advantage: High Temperature Resistant;
Acid: Strong;
Name: Refractory Material;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Powder;
Material: Alumina Cement;
Application: Melting Aluminium Furnace;
Function: Functional Refractory Material;
Al2O3: 65%;
Name: Refractory Castable;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials, Hot Sale;
Type: Refractory Material;
Shape: Brick;
Material: Silicon Carbide (SiC);
Product Name: Silica Bricks;
Processing Service: Bending, Welding, Punching, DEC;
Refractoriness °c: 1790;
Refractoriness Under Load T1,°c: 1650;
Apparent Porosity %: 22-24;
True Density g/cm3: 2.33;
Cold Crushing Strength(MPa): ≥24.5;
Application: Metallurgy;
Standard Size: 230X114X65;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials, Hot Sale;
Type: Refractory Material;
Shape: Brick;
Material: Silicon Carbide (SiC);
Product Name: Silica Bricks;
Processing Service: Bending, Welding, Punching, DEC;
Refractoriness °c: 1790;
Refractoriness Under Load T1,°c: 1650;
Apparent Porosity %: 22-24;
True Density g/cm3: 2.33;
Cold Crushing Strength(MPa): ≥24.5;
Application: Metallurgy;
Standard Size: 230X114X65;
|