Specification |
Type: Oriented Silicon Steel;
Standard: GB, AISI, ASTM, DIN, JIS;
Technique: Cold Rolled;
Shape: Coil;
Technology: Cold Rolled;
Edge: Slit Edge;
Packing: Standard Seaworthy Package;
Coil Weight: 2-5t;
Delivery Time: Within 15 Days;
Monthly Output: 1000t;
Product: Silicon Steel Coil and Sheets;
Coating: C1, C2, C3, C4, C5, C6;
Size: Any Size Are Acceptable;
Market: Asia, Europe, South America;
Thickness: 0.20, 0.23, 0.27, 0.30;
Grade: 065-120;
Width: 900-1200;
Quality: 1st Quality;
|
Type: Oriented Silicon Steel;
Standard: GB, AISI, ASTM, DIN, BS, JIS;
Technique: Cold Rolled;
Shape: Steel Coil;
ID: 508mm;
Nominal Thickness: 0.15-0.30;
Annealing Temperature: 820±20ºC;
Annealing Time: 1.5 to 2.5 Hours;
The Rate of Heating and Cooling: Rapid Heating or Cooling Should Be Forbidden;
Annealing Atmosphere: Nitriding and Oxidation Atmosphere Must Be Avoided;
Nominal Width: 900~1200mm;
Weight: 2~5t;
|
Type: Non-oriented Silicon Steel;
Standard: GB, AISI, ASTM, DIN, BS, JIS;
Technique: Cold Rolled;
Shape: Steel Coil;
ID: 508mm;
Nominal Thickness: 0.10mm,0.12mm,0.15mm,0.17mm;
Annealing Temperature: 820±20ºC;
Annealing Time: 1.5 to 2.5 Hours;
The Rate of Heating and Cooling: Rapid Heating or Cooling Should Be Forbidden;
Annealing Atmosphere: Nitriding and Oxidation Atmosphere Must Be Avoided;
Nominal Width: 200~1500mm;
Weight: 3~8t;
|
Type: Non-oriented Silicon Steel;
Standard: GB, AISI, ASTM, DIN, BS, JIS;
Technique: Cold Rolled;
Shape: Steel Coil;
ID: 508mm;
Nominal Thickness: 0.10mm,0.12mm,0.15mm,0.17mm;
Annealing Temperature: 820±20ºC;
Annealing Time: 1.5 to 2.5 Hours;
The Rate of Heating and Cooling: Rapid Heating or Cooling Should Be Forbidden;
Annealing Atmosphere: Nitriding and Oxidation Atmosphere Must Be Avoided;
Nominal Width: 200~1500mm;
Weight: 3~8t;
|
Type: Non-oriented Silicon Steel;
Standard: GB, AISI, ASTM, DIN, BS, JIS;
Technique: Cold Rolled;
Shape: Steel Coil;
ID: 508mm;
Nominal Thickness: 0.10mm,0.12mm,0.15mm,0.17mm;
Annealing Temperature: 820±20ºC;
Annealing Time: 1.5 to 2.5 Hours;
The Rate of Heating and Cooling: Rapid Heating or Cooling Should Be Forbidden;
Annealing Atmosphere: Nitriding and Oxidation Atmosphere Must Be Avoided;
Nominal Width: 200~1500mm;
Weight: 3~8t;
|