Specification |
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Al2O3%: 48-80;
Fire Resistance: ≥1690°c;
Porosity: ≤25%;
Normal Temperature Compressive Strength: ≥40-60MPa;
Rate of Change of Refiring Line: -0.1-+0.3(1500°c×2h)%;
Load Softening Onset Temperature: ≥1600°c;
Bulk Density: ≥2.50(2.45);
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Synthetic Material;
Application Area: Preheating Zone/Safety Zone;
Bulk Density: 2.2;
Apparent Porosity%: 16;
Tsr: 16 Cycle;
CCS: 57;
Alkali Resistance: 1st Grade;
Size: Customer Made;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Bone Ash;
Size: 6A, 7A, 7as, 7al, 8A and 9 ;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magnesia-Alumina;
Application Zone: Transition Zone;
Bulk Density: 2.9;
Apparent Porosity: 16;
Tsr: 100;
Rul: 1000;
CCS: 65;
Thermal Conductivity: 3.713;
|
Refractoriness (℃): Refractoriness> 2000;
Feature: Long Time Materials;
Type: Heat-Resistant Material;
Shape: Rod;
Material: Alumina;
Size: Diameter 3.4,5.6,7,to 200mm;
Color: White ,Pink,Cream;
Purpose: Insulation,High Temperature Resistance,Stirrer;
Finish: Bore,Polish;
Purity: 99.8%,99.5%,99%,85%,75% Alumina;
|