Specification |
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 67-85;
Density,g/cm3: 1.2;
100% Modulus,MPa: 2-5;
300% Modulus,MPa: 4-10;
Tensile Strength,MPa: 20-35;
Tear Strength,MPa: 65-90;
Elongation at Break,%: 600-700;
Tear Strength,Kn/M: 65-90;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 67-85;
Density,g/cm3: 1.2;
100% Modulus,MPa: 2-5;
300% Modulus,MPa: 4-10;
Tensile Strength,MPa: 20-35;
Tear Strength,MPa: 65-90;
Elongation at Break,%: 600-700;
Tear Strength,Kn/M: 65-90;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 67-85;
Density,g/cm3: 1.2;
100% Modulus,MPa: 2-5;
300% Modulus,MPa: 4-10;
Tensile Strength,MPa: 20-35;
Tear Strength,MPa: 65-90;
Elongation at Break,%: 600-700;
Tear Strength,Kn/M: 65-90;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 82-96;
Density,g/cm3: 1.12;
100% Modulus,MPa: 7-10;
300% Modulus,MPa: 14-19;
Tensile Strength,MPa: 38-50;
Tear Strength,MPa: 90-130;
Elongation at Break,%: 350-500;
Tear Strength,Kn/M: 90-130;
|