Specification |
Molecular Principal Chain: Carbon Chain Polymer;
Color: Light Pink Liquid;
Viscosity (25ºC): 150-300mPa·s;
Gel time(25ºC): 20.0-50.0min;
|
CAS No.: 9009-54-5;
EINECS: 210-898-8;
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 83-96;
Density,g/cm3: 1.07-1.14;
100% Modulus,MPa: 5-10;
300% Modulus,MPa: 10-25;
Tensile Strength,MPa: 30-45;
Tear Strength,MPa: 77-120;
Procesing Temperature,°c: 165-180;
|
CAS No.: 9009-54-5;
EINECS: 210-898-8;
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 63-86;
Density,g/cm3: 1.06-1.12;
100% Modulus,MPa: 2.5-6;
300% Modulus,MPa: 4-10;
Tensile Strength,MPa: 9-20;
Tear Strength,MPa: 35-75;
Elongation at Break,%: 700-950;
Tear Strength,Kn/M: 35-75;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 75-97;
Density,g/cm3: 1.2;
Tensile Strength,MPa: 15-35;
Elongation at Break,%: 450-700;
Tack Free Time,Min: 2-10;
|
CAS No.: 9009-54-5;
EINECS: 210-898-8;
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 43-50;
Density,g/cm3: 0.2-0.23;
Tensile Strength,MPa: 1.3;
Elongation at Break,%: 170;
Tear Strength,Kn/M: 15;
Rebounding,%: 58;
Compression Set(50% 6h, 45ºC),%: 10-15;
|