Specification |
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Purity: 60%;
Alloy: Alloy;
Type: Resistance Alloy;
Powder: Not Powder;
The Highest Use Temperature: 1150c;
Resisivity: 1.11;
Density: 8.2g/cm3;
Sample: Free;
Surface: Bright or Black Skin;
Packing: Standard;
OEM: Yes;
Tensile Strength: 730;
Yield Strength: 370;
|
Application: Industrial;
Standard: JIS, GB, DIN, ASTM;
Alloy: Alloy;
Type: Nickel Strip;
Powder: Not Powder;
Surface: Bright;
Condition: Hard (Y)/ Soft (M)/Half Hard;
Equal to: Hyra 80;
Resistivity: 0.55;
Density(g/cm3): 8.6g/cm3;
Elongation (≥ %): 15-25;
Grade: 1j79;
Feature: High Initial Permeability;
Ni (Min): 80;
|
Application: Industrial;
Standard: JIS, GB, DIN, ASTM;
Alloy: Alloy;
Type: Nickel Wire;
Powder: Not Powder;
Surface: Bright;
Condition: Hard (Y)/ Soft (M)/Half Hard;
Equal to: Hyra 80;
Resistivity: 0.55;
Density(g/cm3): 8.7g/cm3;
Elongation (≥ %): 15-25;
Grade: 1j79;
Feature: High Initial Permeability;
Ni (Min): 80;
|
Application: Electronics, Industrial;
Standard: JIS, GB, DIN, ASTM;
Alloy: Alloy;
Type: Nickel Wire;
Powder: Not Powder;
Surface: Bright;
Treatment: Hydrogen Annealing;
Tensile Strength, Ultimate, Annealed: 827 MPa;
Size: 0.018mm-10.0mm;
Density ( @ 20.0° C/ 68.0° F): 8.10 G/Cm;
Conductor Material: Ni-Cr-Al-Fe;
Resistivity: 1.33±0.07;
Melting Point: 1350° C;
Resistance: 800 Ohm-CIR-Mil/FT or 0.000134 Ohm-Cm;
Composition: Nickel: 75%, Chromium 20%, Aluminium: 2.5%, Copper;
|
Application: Electronics, Industrial;
Standard: JIS, GB, DIN, ASTM;
Alloy: Alloy;
Type: Nickel Wire;
Powder: Not Powder;
Surface: Bright;
Treatment: Hydrogen Annealing;
Tensile Strength, Ultimate, Annealed: 827 MPa;
Size: 0.018mm-10.0mm;
Density ( @ 20.0° C/ 68.0° F): 8.10 G/Cm;
Conductor Material: Ni-Cr-Al-Fe;
Resistivity: 1.33±0.07;
Melting Point: 1350° C;
Resistance: 800 Ohm-CIR-Mil/FT or 0.000134 Ohm-Cm;
Composition: Nickel: 75%, Chromium 20%, Aluminium: 2.5%, Copper;
|