Specification |
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, ASTM;
Purity: 60%;
Alloy: Alloy;
Type: Nickel Wire;
Powder: Not Powder;
Chemical Composition: 56%Ni;
Product Name: Nichrome Resistance Precision Alloy Rod;
Characteristics: High Resistivity, Good Oxidation Resistance;
Melting Point: 1400;
Density: 8. 2g/cm3;
Electrical Resistivity: 1.12 Ohm mm2/M;
Elongation: >=20%;
Hardness: 180 Hv;
Max Working Temperature: 1150 C;
Range of Application: Resistor, Heater;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Purity: >99.99%;
Alloy: Alloy;
Type: Nickel Pipe;
Powder: Not Powder;
Surface: Bright;
Density: 8.1G/M3;
Melting Point: 1430;
Technique: Cold Drawing;
Treatment: Hydrogen Annealing;
Condition: Soft Annealed;
MOQ: 1kg;
Grade: Pure Nickel, Nickel 200;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Purity: 72%;
Alloy: Alloy;
Type: Nickel Bar;
Powder: Not Powder;
Product Name: Nickel-Based Alloy;
Resistance (μΩ.M): According to Standards;
Powder or Not: Not Powder;
Ultimate Strength (≥ MPa): 99;
Elongation (≥ %): 15-25;
Ni (Min): 72%;
Model Number: Hastelloy C276 C22 Inconel 718 625;
Inconel: Inconel 718 625 600 X750;
Hastelloy: C276 C22 X C;
Monel: Monel 400 K500;
Incoloy: Incoloy 800 825;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical, Chemical Industry;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Purity: Ni (Min)63%;
Alloy: Alloy;
Type: Nickel Pipe;
Powder: Not Powder;
Grade: Nickel Base Alloy;
Ni (Min): 58%;
Model Number: Monel 400;
Composition: Ni Min63%, Cu 28%-34%, Fe Max2.5%, Mn Max2%;
Melting: 1300-1390°c;
Density: 8.83 G/M3;
Yield Strength(RP0.2n/mm2): 170;
Hb(≥ ): ≥331;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Alloy: Alloy;
Type: Nickel Pipe;
Powder: Not Powder;
Grade: Nickel, Chromium, Molybdenum, Iron and Titanium;
Model Number: Gh3030 Gh2132 Gh3039 Gh3128 Gh3044;
Material: Gh2747 Pipe;
Density: 8.3G/Cm3;
Melting: 1300-1390°c;
Surface: Bright;
Forging Heating Temperature: 1170~1190ºC;
Elongation: 3.5;
Process Method: Cold Drawn;
|