Specification |
Standard: ASTM;
Surface Treatment: Polishing;
Manufacturing Process: Casting;
Material: High Chrome Cast Iron&Mild Steel;
Name: Chocky Bar;
Size: CB40, CB90, CB130 Wb110, Wb115, Wb150;
Hardness: 63HRC / 700bhn;
Tensile Strength: 630MPa Min;
Shearing Strength: 250MPa Min;
Micro-Structure: Carbide+Martensite+Retained Austenite;
Application: Industrial Equipment Wear Protection;
Synonym: Laminated High Chrome White Iron Chocky Bar for Ex;
Products: 700bhn Bimetallic White Iron Chocky Wear Bars for;
|
After-sales Service: on-Line After Sales Service;
Warranty: 3months;
Standard: ASME, GB;
Surface Treatment: Sand Blast;
Manufacturing Process: Forging;
Material: Alloy Steel;
Product Name: Bullet Teeth;
Size: Standard Size;
Packing: Plastic Box+Wooden Case;
Steel Grade: 42CrMo;
Advantage: Wear Resitant;
Weight: 0.5 Kg;
|
After-sales Service: on-Line After Sales Service;
Warranty: 3months;
Standard: ASME, GB;
Surface Treatment: Sand Blast;
Manufacturing Process: Forging;
Material: Alloy Steel;
Product Name: Bullet Teeth;
Size: Standard Size;
Packing: Plastic Box+Wooden Case;
Steel Grade: 42CrMo;
Advantage: Wear Resitant;
Weight: 0.5 Kg;
|
Surface Treatment: Spray-Paint;
Manufacturing Process: Forging;
Material: Alloy Steel;
Connection Thread: API 3 1/2" Reg;
Hole Range: Dia 155 - 190 mm;
Working Pressure: 1.0 - 2.5MPa;
Compatible Bit Shank: Cop64, DHD360, Ql60, M60, SD6, CD65;
|
After-sales Service: on-Line After Sales Service;
Warranty: 3months;
Standard: ASME, GB;
Surface Treatment: Sand Blast;
Manufacturing Process: Forging;
Material: Alloy Steel;
Product Name: Bullet Teeth;
Size: Standard Size;
Packing: Plastic Box+Wooden Case;
Steel Grade: 42CrMo;
Advantage: Wear Resitant;
Weight: 0.5 Kg;
|