Specification |
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Needle;
Kind: High Purity Ceramic Fiber;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃, 1360;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Plate;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Specification Temp: 1260/1360/1430;
Certifiacte: ISO9001, Ce, etc;
Width: Customizable;
Bulk Density(g/cm3): 280-350;
Thickness: 4-110mm;
Al2O3: 38-45;
Al2O3+Sio2: 96-99;
Tensile Strength: 0.2;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃;
Chemical Composition:: Al2O3.SiO2, Al2O3+Sio2+Zro2;
Shape: Ceramic Fiber Module;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Specification Temp: 1260/1350/1430;
Certifiacte: ISO9001, Ce, etc;
Linear Shrinkage After Heating: 1000ºC*24h<=2.5-3.5;
Bulk Density(g/cm3): 180-240;
Thermal Conductivity: 0.09-0.175;
Al2O3: 34-45%;
Sio2: 50-54%;
Zro2: 15%;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃;
Chemical Composition:: Al2O3.SiO2, Al2O3+Sio2+Zro2;
Shape: Ceramic Fiber Module;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Specification Temp: 1260/1350/1430;
Certifiacte: ISO9001, Ce, etc;
Linear Shrinkage After Heating: 1000ºC*24h<=2.5-3.5;
Bulk Density(g/cm3): 180-240;
Thermal Conductivity: 0.09-0.175;
Al2O3: 34-45%;
Sio2: 50-54%;
Zro2: 15%;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃;
Chemical Composition:: Al2O3.SiO2, Al2O3+Sio2+Zro2;
Shape: Ceramic Fiber Module;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Specification Temp: 1260/1350/1430;
Certifiacte: ISO9001, Ce, etc;
Linear Shrinkage After Heating: 1000ºC*24h<=2.5-3.5;
Bulk Density(g/cm3): 180-240;
Thermal Conductivity: 0.09-0.175;
Al2O3: 34-45%;
Sio2: 50-54%;
Zro2: 15%;
|