Specification |
Refractoriness (℃): 1050-1800c;
Feature: Long Time Materials;
Type: Heat-Resistant Material;
Shape: Module;
|
Refractoriness (℃): 1200 Celsius Degree;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Rectangle, Round, Square;
Material: Alumina;
Specification: Diameter=30~500mm H=5~20mm;
Ppi: 10ppi, 20ppi, 30ppi, 40ppi, 50ppi, 60ppi;
Thickness: 12-25mm;
Usage: Alumina Alloy Casting;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Magnesium Oxide Boards;
Shape: Plate;
Material: MgO-Carbon Brick;
Color: White, Grey, Red, Green;
Density: 1.0-1.2g/cm3(GB/T-7019-1997);
Fire Ratings: A1 Grade (GB 8624);
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Magnesium Oxide Boards;
Shape: Plate;
Material: MgO-Carbon Brick;
Color: White, Grey, Red, Green;
Density: 1.0-1.2g/cm3(GB/T-7019-1997);
Fire Ratings: A1 Grade (GB 8624);
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magnesia-Hecynite;
Application Area: burning and transition Zone in Rotary Kiln;
Size: Customer Made;
Bulk Density: 2.9-3.0g/cm3;
Apparent Porosity: 16%;
Tsr 950ºC: 100 Cycle;
Rul: 1700ºC;
CCS MPa: 60;
MGO: 85-87;
Standard: VDZ/ISO;
|