| Specification |
Refractoriness (℃): 1260c, 1360c, 1400c;
Feature: Long Time Materials;
Type: Heat-Resistant Material;
Shape: Ceramic Fiber Module;
Material: Al2O3+Sio2;
|
Refractoriness (℃): 1380;
Feature: Long Time Materials;
Type: Heat-Resistant Material;
Shape: Pipe;
Material: Silicon Carbide (SiC);
colour: Dark-gray;
model number: SISIC;
SiC Content (%): 83.66%;
Density: under 3.02 g/cm3;
Open Porosity: <0.1%;
Bending strength: 250MPa/280MPa;
Modulus of Elastictiy: 330Gpa/300Gpa;
Thermal Conductivity: 45W/m.K(1200 Celsius);
Coefficiant of Thermal Expansion: 4.5K-1*10-6;
Moh"s Hardness: 9.15;
Vickers Hardness HV: 20Gpa;
Acid Alkaline-proof: Excellent;
Size: Customer's Required;
|
colour: Dark-gray;
model number: SISIC;
SiC Content (%): 83.66%;
Density: under 3.02 g/cm3;
Open Porosity: <0.1%;
Bending strength: 250MPa/280MPa;
Modulus of Elastictiy: 330Gpa/300Gpa;
Thermal Conductivity: 45W/m.K(1200 Celsius);
Coefficiant of Thermal Expansion: 4.5K-1*10-6;
Moh"s Hardness: 9.15;
Vickers Hardness HV: 20Gpa;
Acid Alkaline-proof: Excellent;
Length: Customer's Required;
Flange Width: Customer's Required;
Thickness: Customer's Required;
|
colour: Dark-gray;
model number: SISIC;
SiC Content (%): 83.66%;
Density: under 3.02 g/cm3;
Open Porosity: <0.1%;
Bending strength: 250MPa/280MPa;
Modulus of Elastictiy: 330Gpa/300Gpa;
Thermal Conductivity: 45W/m.K(1200 Celsius);
Coefficiant of Thermal Expansion: 4.5K-1*10-6;
Moh"s Hardness: 9.15;
Vickers Hardness HV: 20Gpa;
Acid Alkaline-proof: Excellent;
Length: Customer's Required;
Flange Width: Customer's Required;
Thickness: Customer's Required;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Long Time Materials, Instant Materials;
Type: Refractory Material, Ceramic Crucible;
Shape: Crucible, Conical, Circular, Cylindrical;
Material: Alumina Cement, Clay;
Refractoriness: 1580< Refractoriness< 1770;
Color: White, Light Yellow;
Name: Ceramic Clay Fire Assay Crucible for Melting Gold;
Max. Working Temperature: 1650 Degree Celsius;
Item: Ceramic Crucible;
Application: Thermal Analysis or Firing;
Capacity: 10ml, 20ml, 30ml, 50ml, 80ml, 100ml, 200ml, 500ml;
Purpose: Gold Smelting and Assaying;
Size: 30g, 40g, 45g, 50g, 65g;
Usage: Melting, Assaying;
Refractoriness Under Load: 1420 Degree Celsius;
Packing: Wooden Packing, Paper Carton Packing;
|