Specification |
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Plate;
Manufacturing Technique: Vacuum Forming;
Kind: Refractory Material;
|
Usage: Friction Material, High Temperature Insulating Material;
Temprature Classification: 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Blanket;
Manufacturing Technique: Jilt Silk Rug;
Kind: High Purity Ceramic Fiber;
Product Name: Ceramic Fibre Module;
Application: Refractory;
Thickness: Customizable;
Width: Customizable;
Length: Customizable;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.04;
Working Temperature: 1000-1350;
Fiber Diameter: 3-5um;
Shrinkage (1800 ºF, 3h): 3%(24 Hours);
Thermal Conductivity: 0.055-0.180(W.K.M.);
Density (Kg/M³ ): 160;
Color: Pure White;
|
Usage: Friction Material, High Temperature Insulating Material;
Temprature Classification: 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Blanket;
Manufacturing Technique: Jilt Silk Rug;
Kind: High Purity Ceramic Fiber;
Product Name: Ceramic Fibre Module;
Application: Refractory;
Thickness: Customizable;
Width: Customizable;
Length: Customizable;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.04;
Working Temperature: 1000-1350;
Fiber Diameter: 3-5um;
Shrinkage (1800 ºF, 3h): 3%(24 Hours);
Thermal Conductivity: 0.055-0.180(W.K.M.);
Density (Kg/M³ ): 160;
Color: Pure White;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1050~1600 C.Degree;
Chemical Composition:: Al2O3+Sio2≥99%;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Ceramic Fiber Bulk Wool;
Kind: Ordinary Ceramic Fiber;
Thickness: 6mm-50mm, 1", 1/2"2";
Ultimate Strength (≥ MPa): 0.5MPa (25mm Thickness);
Fiber Diameter: 3-5μm;
Thermal Conductivity: 0.06-0.12;
Classification Temperature: 1200;
Ttensile Strenghth(_Kpa): 30/50/70;
Width: 100mm-1220mm;
Shrinkage (1800 ºF, 3h): 1050~1600 C.Degree;
Density (Kg/M³ ): 128;
Al2O3: ≥43;
Zro2: ≥54;
Permanent Linear Shrinkage: 1000c*24HS2.5;
Density: 64/96/128;
|
Usage: Friction Material, High Temperature Insulating Material;
Temprature Classification: 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Blanket;
Manufacturing Technique: Jilt Silk Rug;
Kind: High Purity Ceramic Fiber;
Product Name: Ceramic Fibre Module;
Application: Refractory;
Thickness: Customizable;
Width: Customizable;
Length: Customizable;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.04;
Working Temperature: 1000-1350;
Fiber Diameter: 3-5um;
Shrinkage (1800 ºF, 3h): 3%(24 Hours);
Thermal Conductivity: 0.055-0.180(W.K.M.);
Density (Kg/M³ ): 160;
Color: Pure White;
|