Specification |
Refractoriness (℃): 1050-1800c;
Feature: Long Time Materials;
Type: Heat-Resistant Material;
Shape: Module;
|
Refractoriness (℃): 800-1500;
Feature: Long Time Materials;
Type: Heat-Resistant Material;
Shape: Pipe;
Material: Castable;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Pipe;
Material: Alumina Cement;
|
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Long Time Materials;
Production Process: Extrusion Method, Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770, 1580< Refractoriness< 1770;
Shape: Brick, Brick;
Type: Refractory Material;
Material: Alumina Block;
Al2O3: 35%~45%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Refractoriness: Sk32-34;
Apparent Porosity: 13-26%;
Bulk Density: 2.25-2.65g/cm3;
Refractoriness Under [email protected]: 1250-1500;
Thermal Linear Expansion@1000deg: 0.6%;
Fe2o3: 1.8-3.0%;
|
Sio2: 95%-96%;
Fe2o3: 0.5%;
Al2O3: 3%;
Bulk Density: 1.8g/cm3;
Refractoriness: 1710c-1730c;
Apparent Porosity: 22%;
Cold Crushing Strength: 29MPa-35MPa;
|