Specification |
Type: Oriented Silicon Steel;
Standard: GB;
Technique: Cold Rolled;
Shape: Lamination Sheet;
Application: Power;
Phase: Three;
Core: Core-Type Transformer;
Cooling Method: Oil-Immersed Type Transformer;
Winding Type: Two-Winding Transformer;
Usage: Power Transformer;
Frequency Characteristics: Power Frequency;
Shape of Core: Ei;
Brand: Shanghai Jisco;
Material: Cold Rolled Oriented Silicon Steel Sheet;
Window Height: According to Requirements;
Stack Thickness: According to Requirements;
Model No.: 30kVA-50000kVA;
Magnetic Flux Density: 1.7t;
Coefficient of Laminated: 0.96-0.975;
|
Type: Non-oriented Silicon Steel;
Standard: GB, AISI, ASTM, DIN, BS, JIS;
Technique: Cold Rolled;
Shape: Steel Coil;
Package: Standard Seaworth Packing;
Application: Power Transformer Core/Motor Core;
Grade: 50ww470/30ww230/50ww800/1300;
Color: Silver Gray;
Supply Type: in-Stock Items;
Steel Shape: CRNGO Electrical Silicon Steel;
Thickness: 0.20mm,0.25mm,0.30mm,0.35mm,0.50mm,0.65mm;
Width: 20mm-1250mm;
|
Type: Non-oriented Silicon Steel;
Standard: GB, AISI, ASTM, DIN, BS, JIS;
Technique: Cold Rolled;
Shape: Steel Coil;
Package: Standard Seaworth Packing;
Application: Power Transformer Core/Motor Core;
Grade: 50ww470/30ww230/50ww800/1300;
Color: Silver Gray;
Supply Type: in-Stock Items;
Steel Shape: CRNGO Electrical Silicon Steel;
Thickness: 0.20mm,0.25mm,0.30mm,0.35mm,0.50mm,0.65mm;
Width: 20mm-1250mm;
|
Type: Oriented Silicon Steel;
Standard: GB, AISI, ASTM, DIN, BS, JIS;
Technique: Cold Rolled;
Shape: Steel Coil;
ID: 508mm;
Nominal Thickness: 0.15-0.30;
Annealing Temperature: 820±20ºC;
Annealing Time: 1.5 to 2.5 Hours;
The Rate of Heating and Cooling: Rapid Heating or Cooling Should Be Forbidden;
Annealing Atmosphere: Nitriding and Oxidation Atmosphere Must Be Avoided;
Nominal Width: 900~1200mm;
Weight: 2~5t;
|
Type: Oriented Silicon Steel;
Standard: GB, AISI, ASTM, DIN, BS, JIS;
Technique: Cold Rolled;
Shape: Steel Coil;
ID: 508mm;
Nominal Thickness: 0.15-0.30;
Annealing Temperature: 820±20ºC;
Annealing Time: 1.5 to 2.5 Hours;
The Rate of Heating and Cooling: Rapid Heating or Cooling Should Be Forbidden;
Annealing Atmosphere: Nitriding and Oxidation Atmosphere Must Be Avoided;
Nominal Width: 900~1200mm;
Weight: 2~5t;
|