Specification |
Usage: High Temperature Insulating Material;
Temprature Classification: 1260℃;
Chemical Composition:: SiO2, Al2O3;
Shape: Ceramic Fiber Board;
Manufacturing Technique: Jilt Silk Rug;
Kind: Ordinary Ceramic Fiber;
Color: White;
Density: 250-300 Kg/M3;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1050~1600 C.Degree;
Chemical Composition:: Al2O3+Sio2≥99%;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Ceramic Fiber Bulk Wool;
Kind: Ordinary Ceramic Fiber;
Thickness: 6mm-50mm, 1", 1/2"2";
Ultimate Strength (≥ MPa): 0.5MPa (25mm Thickness);
Fiber Diameter: 3-5μm;
Thermal Conductivity: 0.06-0.12;
Classification Temperature: 1200;
Ttensile Strenghth(_Kpa): 30/50/70;
Width: 100mm-1220mm;
Shrinkage (1800 ºF, 3h): 1050~1600 C.Degree;
Density (Kg/M³ ): 128;
Al2O3: ≥43;
Zro2: ≥54;
Permanent Linear Shrinkage: 1000c*24HS2.5;
Density: 64/96/128;
|
Usage: Friction Material, High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Blanket;
Product Name: Ceramic Fiber Blanket;
Application: Refractory;
Thickness: 10-50mm;
Width: 610/1220mm;
Length: 3600/7200/14640mm, 7200-3600;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.04;
Working Temperature: 1000-1350;
Fiber Diameter: 3-5um;
Shrinkage (1800 ºF, 3h): 3%(24 Hours);
Thermal Conductivity: 0.055-0.180(W.K.M.);
Density (Kg/M³ ): 160;
Color: Pure White;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Paper;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Specification Temp: 1000/1100/1300;
Certifiacte: ISO9001, CE, etc;
Width: 610mm 1220mm;
Bulk Density(g/cm3): 200;
Thickness: 0.5-10mm;
Al2O3: 40-48;
Sio2: 51-52;
Tensile Strength: 0.4;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2, Al2O3+Sio2+Zro2;
Shape: Ceramic Fiber Tube;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Bulk Density(g/cm3): 400;
Fiber Diamete: 3-5um;
Thermal Conductivity: 0.075;
Working Temperature: 1050 --1350;
Raw Material: Aluminum Silicate;
Diameter: 5-100mm;
Color: White;
|