Specification |
Usage: High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Paper;
Manufacturing Technique: Jilt Silk Rug;
Kind: Ordinary Ceramic Fiber;
Color: White;
Density: 190kg/M3;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Plate;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Bulk Density: 320kg/M3;
Specific Heat Capacity(: 0.8kj/Kg.K;
Compressive Strength: 0.3MPa;
Linear Shrinkage(800ºC): 2.0%;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1050℃, 650ºC;
Chemical Composition:: Calcium, Magnesium, Silicate Chemistry;
Shape: Braid Rope;
Manufacturing Technique: Spray Silk Rug;
Kind: Bio-Soluble Fiber;
Color: Green;
Standard Densities: 600-650 Kg/M3;
Reinforced Material: Fiberglass or Stainless Steel;
Customized Service: Yes, Width/Thickness Can Be Customized;
Thermal Shock Resistance: Good;
Features: Light Weight, Low Heat Storage, etc.;
Application: Gaskets, Seals, Pipe Wrap, etc.;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1050℃, 650ºC;
Chemical Composition:: Calcium, Magnesium, Silicate Chemistry;
Shape: Ceramic Fiber Textile;
Manufacturing Technique: Spray Silk Rug;
Kind: Bio-Soluble Fiber;
Color: Green;
Standard Densities: 500 Kg/M3;
Thickness: Tape/Cloth: 2-6mm;
Reinforced Material: Fiberglass or Stainless Steel;
Thermal Shock Resistance: Good;
Features: Light Weight, Low Heat Storage, etc.;
Application: Radiant Heat Fields, Pipe Wrap, Welding, etc.;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Plate;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Bulk Density: 320kg/M3;
Specific Heat Capacity(: 0.8kj/Kg.K;
Compressive Strength: 0.3MPa;
Linear Shrinkage(800ºC): 2.0%;
|