Specification |
Usage: High Temperature Insulating Material;
Temprature Classification: 1500℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Paper;
Manufacturing Technique: Jilt Silk Rug;
Kind: Ordinary Ceramic Fiber;
Density: 180-220 Kg/M3;
Color: White;
Classification Temperature: 1400ºC;
|
Usage: Iron Voltage Electric Material, Thermal Insulation Coatings, Friction Material, Packing Material, Filter Material, High Temperature Insulating Material;
Temprature Classification: 1900℃, 1600℃, 1500℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Fiber Granules;
Manufacturing Technique: Jilt Silk Rug;
Kind: Ordinary Ceramic Fiber;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1260℃, 1050℃, 1430;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Specification Temp: 1260/1360/1430;
Certifiacte: ISO9001, CE, etc;
Working Temperature: 1050-1350;
Bulk Density(g/cm3): 96-160;
Linear Shrinkage After Heating: -3;
Thermal Conductivity: 0.09-0.76;
Al2O3: 34-52;
Al2O3+Sio2: 96-99;
Tensile Strength: 0.05-0.06;
|
Usage: Friction Material, High Temperature Insulating Material;
Temprature Classification: 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Blanket;
Product Name: Ceramic Fiber Blanket;
Application: Refractory;
Thickness: 10-50mm;
Width: 610/1220mm;
Length: 3600/7200/14640mm, 7200-3600;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.04;
Working Temperature: 1000-1350;
Fiber Diameter: 3-5um;
Shrinkage (1800 ºF, 3h): 3%(24 Hours);
Thermal Conductivity: 0.055-0.180(W.K.M.);
Density (Kg/M³ ): 160;
Color: Pure White;
|
Usage: Friction Material, High Temperature Insulating Material;
Temprature Classification: 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Blanket;
Product Name: Ceramic Fiber Blanket;
Application: Refractory;
Thickness: 10-50mm;
Width: 610/1220mm;
Length: 3600/7200/14640mm, 7200-3600;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.04;
Working Temperature: 1000-1350;
Fiber Diameter: 3-5um;
Shrinkage (1800 ºF, 3h): 3%(24 Hours);
Thermal Conductivity: 0.055-0.180(W.K.M.);
Density (Kg/M³ ): 160;
Color: Pure White;
|