| Specification |
Feature: Long Time Materials, Instant Materials;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Brick;
Color: White;
Al2O3: 60%;
Sio2: 34%;
Fe2o3: 1.1%;
Type: Heat-Resistant Material;
Material: Alumina Block;
|
Classification: High-Alumina;
Feature: Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight;
Production Process: Sintering Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate;
Tensile Strength: 650MPa;
Erosion in The H2,at 454,Mil/Yr: 21.9;
Carbon Content of The Alloy After Solid: Lower Than 0.30%;
Max Working Temp. in The So2: 1100 Degree;
|
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Extrusion Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Brick;
Usage: Furnace Liner;
Al203 Content (%): 35%-45%;
Si02 Content (%: 52%;
MGO Content (%): 0.1%;
Refractoriness (Degree): Common1580< Refractoriness< 1770;
Cro Content %): 0.1%;
Bulk Density: 2.0~2.2g/cm3;
Sic Content %): 0.1%;
Apparent Porosity: 23%~26%;
Cold Crushing Strength: 20~35MPa;
Cao Content %): 0.1%;
Application: Industrial Furnaces;
Single Package Size: 100X100X110.Cm;
|
Classification: High-Alumina;
Feature: Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight;
Production Process: Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Block;
Tensile Strength: 650MPa;
Erosion in The H2,at 454,Mil/Yr: 21.9;
Carbon Content of The Alloy After Solid: Lower Than 0.30%;
Max Working Temp. in The So2: 1100 Degree;
|
Feature: Long Time Materials;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Nano-Aggregate;
Product Name: Lightweight Nano-Aggregate;
Working Temperature,ºC: ≥1450;
Brand Name: Rongsheng;
Bd, G/Cm³: ≤1.7;
Application Limit Temp: 1700;
CCS,MPa: ≥50;
Grain Size: Customizable;
Type: Refractory Material;
Material: Mullite;
|