Specification |
Feature: Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, Thermal Shock Resistance, Long Time Materials;
Shape: Brick, Brick;
Refractoriness (℃): 1770< Refractoriness< 2000;
Type: Refractory Material;
Material: Alumina Block;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 7-9%;
Cold Crushing Strength: 45-55MPa;
Refractoriness Under Load: 1550-1700;
Al2O3: 65-72%;
Sic: 10-11%;
FC: 10-13%;
|
Feature: Instant Materials;
Product Name: Thermal Analysis Carbon Cup;
Temperature Range: 1250-1370;
Carbon Equivalen: 3.2%-4.8%;
Carbon Content: 2.3%-4.2%;
Silicon Content: 0.6%-3.8%;
Types: Round and Square Type;
Measurement Function: Thermal Analysis Towards Cast Iron;
Measuring Time: 240 Seconds at Most;
Refractoriness (℃): 1580< Refractoriness< 1770;
Type: Refractory Material;
|
Feature: Long Time Materials, Instant Materials;
Shape: Plate;
Product Name: Thermal Analysis Carbon Cup;
Temperature Range: 1250-1370;
Carbon Equivalen: 3.2%-4.8%;
Carbon Content: 2.3%-4.2%;
Silicon Content: 0.6%-3.8%;
Types: Round and Square Type;
Measurement Function: Thermal Analysis Towards Cast Iron;
Measuring Time: 240 Seconds at Most;
Refractoriness (℃): 1580< Refractoriness< 1770;
Type: Calcium Silicate Boards;
Material: MgO-Carbon Brick;
|
Feature: Long Time Materials, Instant Materials;
Shape: Brick;
Product Name: Thermal Analysis Carbon Cup;
Temperature Range: 1250-1370;
Carbon Equivalen: 3.2%-4.8%;
Carbon Content: 2.3%-4.2%;
Silicon Content: 0.6%-3.8%;
Types: Round and Square Type;
Measurement Function: Thermal Analysis Towards Cast Iron;
Measuring Time: 240 Seconds at Most;
Refractoriness (℃): 1580< Refractoriness< 1770;
Type: Refractory Material;
Material: Alumina Block;
|
Feature: Long Time Materials, Instant Materials;
Shape: Pipe;
Product Name: Thermal Analysis Carbon Cup;
Temperature Range: 1250-1370;
Carbon Equivalen: 3.2%-4.8%;
Carbon Content: 2.3%-4.2%;
Silicon Content: 0.6%-3.8%;
Types: Round and Square Type;
Measurement Function: Thermal Analysis Towards Cast Iron;
Measuring Time: 240 Seconds at Most;
Refractoriness (℃): 1770< Refractoriness< 2000;
Type: Ablative Material;
Material: Castable;
|