| Specification |
Usage: High Temperature Insulating Material;
Chemical Composition:: Al2O3.SiO2;
Manufacturing Technique: Spray Silk Rug;
Bulk Density: 60-200kg/M3;
Thermal Conductivity: 0.044W/M.K @70c;
Shot Content: 12%;
Fiber Mean Value: 7um;
Water Content: 0.5%;
Combustibility: A Grade Nonflammable;
Organic Content: 4.0%;
Hydrophobicity: 98%;
Water Absorption: 5%;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1050~1600 C.Degree;
Chemical Composition:: Al2O3+Sio2≥99%;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Ceramic Fiber Bulk Wool;
Kind: Ordinary Ceramic Fiber;
Thickness: 10-50mm, 1", 1/2"2";
Ultimate Strength (≥ MPa): MPa): 30/50/70;
Fiber Diameter: 3-5μm;
Thermal Conductivity: 0.06-0.12;
Ttensile Strenghth(_Kpa): 30/50/70;
Width: 600mm, 610mm, 1220mm;
Shrinkage (1800 ºF, 3h): 1050~1600 C.Degree;
Density (Kg/M³ ): 128;
MGO: 4-7%;
Sio2: 62-68%;
Cao: 26-32%;
Density: 64/96/128;
Color: White;
Permanent Linear Shrinkage: 1000c*24h<1.0;
|
Usage: Friction Material, High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Product Name: Ceramic Fiber Blanket;
Application: Refractory;
Thickness: 10-50mm;
Width: 610/1220mm;
Length: 3600/7200/14640mm, 7200-3600;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.04;
Working Temperature: 1000-1350;
Fiber Diameter: 3-5um;
Shrinkage (1800 ºF, 3h): 3%(24 Hours);
Thermal Conductivity: 0.055-0.180(W.K.M.);
Density (Kg/M³ ): 160;
Color: Pure White;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Different Shapes;
Manufacturing Technique: Vacuum Formed;
Kind: High Purity Ceramic Fiber;
Shapes: Can Be Made Different Shapes;
Density: 280kg/M3-450kg/M3;
Color: White;
Organic Type: with Smell;
Inorganic Type: Without Smell;
Application: Boiler, Furnace, Stove etc;
Loss of Ignition, Loi, %: <8;
Permanent Linear Shrinkage, %, 24 Hours: <3;
Compressive Strength: >0.2;
Thermal Conductivity, W/M•K: 0.06-0.18;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Different Shapes;
Manufacturing Technique: Vacuum Formed;
Kind: High Purity Ceramic Fiber;
Shapes: Can Be Made Different Shapes;
Density: 280kg/M3-450kg/M3;
Color: White;
Organic Type: with Smell;
Inorganic Type: Without Smell;
Application: Boiler, Furnace, Stove etc;
Loss of Ignition, Loi, %: <8;
Permanent Linear Shrinkage, %, 24 Hours: <3;
Compressive Strength: >0.2;
Thermal Conductivity, W/M•K: 0.06-0.18;
|