Specification |
Usage: High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Cotton;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Specification Temp: 1260c,1430c;
Certifiacte: ISO9001, CE, etc;
Shot Content (%): 12-15;
Al2O3: 34-44;
Sio2: 50-52;
Fiber Diameter(μm): 3.5;
|
Usage: Friction Material, High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Product Name: Ceramic Insulation Blanket;
Application: Refractory;
Thickness: 10-50mm;
Width: 610/1220mm;
Length: 3600/7200/14640mm, 7200-3600;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.04;
Working Temperature: 1000-1350;
Fiber Diameter: 3-5um;
Shrinkage (1800 ºF, 3h): 3%(24 Hours);
Thermal Conductivity: 0.055-0.180(W.K.M.);
Density (Kg/M³ ): 160;
Color: Pure White;
|
Usage: Friction Material, High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Product Name: Ceramic Insulation Blanket;
Application: Refractory;
Thickness: 10-50mm;
Width: 610/1220mm;
Length: 3600/7200/14640mm, 7200-3600;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.04;
Working Temperature: 1000-1350;
Fiber Diameter: 3-5um;
Shrinkage (1800 ºF, 3h): 3%(24 Hours);
Thermal Conductivity: 0.055-0.180(W.K.M.);
Density (Kg/M³ ): 160;
Color: Pure White;
|
Usage: Friction Material, High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Product Name: Ceramic Insulation Blanket;
Application: Refractory;
Thickness: 10-50mm;
Width: 610/1220mm;
Length: 3600/7200/14640mm, 7200-3600;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.04;
Working Temperature: 1000-1350;
Fiber Diameter: 3-5um;
Shrinkage (1800 ºF, 3h): 3%(24 Hours);
Thermal Conductivity: 0.055-0.180(W.K.M.);
Density (Kg/M³ ): 160;
Color: Pure White;
|
Usage: Friction Material, High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Product Name: Ceramic Insulation Blanket;
Application: Refractory;
Thickness: 10-50mm;
Width: 610/1220mm;
Length: 3600/7200/14640mm, 7200-3600;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.04;
Working Temperature: 1000-1350;
Fiber Diameter: 3-5um;
Shrinkage (1800 ºF, 3h): 3%(24 Hours);
Thermal Conductivity: 0.055-0.180(W.K.M.);
Density (Kg/M³ ): 160;
Color: Pure White;
|