Specification |
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Low Thermal Conductivity, Permeability, Thermal Shock Resistance, Long Time Materials;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate, Plate;
Type: Calcium Silicate Boards;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Bulk Density: 230;
Compressive Strength: 0.52-0.6MPa;
Thermal Conductivity: 0.05-0.062W/M.K;
Specification Temp: 1050/650;
Bending Strength: 0.3-0.45;
Sio2: 43%;
Cao: 44%;
|
Feature: Good Acid Resistance, High Refractoriness, Thermal Shock Resistance;
Production Process: Dry Pressing;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Brick;
Type: Silica Brick;
Sio2 Brick: Min94%;
Application: Glass Furnace;
Refractory Material: Fireproof Material;
Character: Good Acids Resistance;
|
Feature: High Refractoriness, Thermal Shock Resistance;
Production Process: Dry Pressing;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Brick;
Type: Silica Brick;
Sio2 Brick: Min94%;
Application: Glass Furnace;
Refractory Material: Fireproof Material;
Character: Silica Brick;
|
Feature: Good Acid Resistance, High Refractoriness, Thermal Shock Resistance, Volume Stability;
Production Process: Dry Pressing;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Brick;
Type: Silica Brick;
Sio2: Min95%;
Application: Industrial Blast Furnace;
Brick: Refractory Brick;
Refractory Material: Fireproof Material;
Sio2 Brick: Silica Brick;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Brick;
Sio2: 89%~92%;
Bulk Density: 0.6g/cm3~0.8g/cm3;
|