Specification |
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Long Time Materials;
Refractoriness (℃): 1580< Refractoriness< 1770, 1770< Refractoriness< 2000;
Shape: Powder, Powder;
Type: Refractory Material;
Material: Castable;
Al2O3: 45-95%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Application Limit Temp: 1400-1800ºC;
CCS/Mor: 14-60MPa;
Bulk Density: 2.0-3.0g/cm3;
Thermal Conductivity: 0.6-1.1W/M.K;
Cao: 2-3;
|
Density: 220;
Width: 300 mm or Customized;
Item: Ceramic Fiber Module;
Color: White/ Pure White;
|
Classification: High-Alumina;
Feature: High-Temperature Resistant;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Grit / Powder/ Grain;
Used: Refractory Stone, Castable, Nozzle Material;
Color: White;
Name: White Fused Alumina;
Customized: OEM/ODM;
Other Name: White Corundum;
Nao2: <0.4;
Hardness: Superabrasive;
|
Al2O3: 40-70%;
Fe2o3: 0.5-2.0%;
Bulk Density: 0.6-1.1 g/cm3;
Product Name: Insulating Brick;
Certifiacte: ISO9001, CE, etc;
Cold Crushing Strength: 1-3 MPa;
Classification Temperature: 1200~1600ºC;
Application: Industrial Furnace;
Performance: Excellent;
Grade: Jm23/Jm26/Jm28/Jm30/Jm32;
Thermal Conductivity: Low;
Color: White;
Size Control: Accurate;
Production Time: 15-30 Days;
Testing Laboratory: Support;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Stirring Processing;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Powder;
Item: Refractory Castable;
Bulk Density: 2.2-2.7 g/cm3;
Color: Grey, White;
Application: Industrial Furnaces;
Advantage: High Temperature Resistant;
Service Tempera: 1200-1700 ºC;
Cold Crushing Strength: 40-80 MPa;
Chemical Analysis: Al2O3/Cao/Fe2o3;
Production Time: 15-30 Days;
Customized: Acceptable;
Testing Laboratory: Support;
Thermal Shock Resistance: Excellent;
Quality Assurance: Yes;
Performance: Excellent;
|