Specification |
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Silicon Carbide (SiC);
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 16-22%;
Cold Crushing Strength: 80-130MPa;
Refractoriness Under Load: 1550-1700;
Fe2o3: 0.3-1.0%;
Sick: 73-90%;
Si3n4: 0-25;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Block;
Material: Alumina Block;
Product Number: Azs Refractory Brick;
Brand Name: Rongsheng;
Zro2 Content(%): ≥40;
Na2o Content(%): ≤1.3;
Keyword: Fused Azs Block;
Fe2o3+TiO2 Content(%): ≤0.3;
Bulk Density(g/cm3): ≤3.9;
Density: ≤3.8;
Application: Glass Kiln;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials, High Temperature Resistance;
Type: Refractory Material;
Shape: Brick;
Material: Magsite;
Keyword: Magnesia Block Refractory Bricks;
Size of Basic Refractory: 230*114*65mm or Special S;
Refractoriness: Super-Class (Refractoriness> 2000;
Apparent Porosity: Max 16%;
Applications: Iron Steel Furnace,Glass Furnace,Ceme;
Refractory Brick Feature: High Refractoriness;
Cold Crushing Strength: Min 60 MPa;
Reheating Linear Change(1650 °c,2h): 0~-0.4;
Advantage: Resist Basic (Alkaline) Slag;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials, High Temperature Resistance;
Type: Refractory Material;
Shape: Brick;
Material: Magsite;
Keyword: Magnesia Block Refractory Bricks;
Size of Basic Refractory: 230*114*65mm or Special S;
Refractoriness: Super-Class (Refractoriness> 2000;
Apparent Porosity: Max 16%;
Applications: Iron Steel Furnace,Glass Furnace,Ceme;
Refractory Brick Feature: High Refractoriness;
Cold Crushing Strength: Min 60 MPa;
Reheating Linear Change(1650 °c,2h): 0~-0.4;
Advantage: Resist Basic (Alkaline) Slag;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Block;
Material: Alumina Block;
Product Number: Azs Refractory Brick;
Brand Name: Rongsheng;
Zro2 Content(%): ≥40;
Na2o Content(%): ≤1.3;
Fe2o3+TiO2 Content(%): ≤0.3;
Bulk Density(g/cm3): ≤3.9;
Density: ≤3.8;
Application: Glass Kiln;
|