Specification |
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Long Time Materials;
Production Process: Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770, 1770< Refractoriness< 2000;
Shape: Brick, Brick;
Type: Refractory Material;
Material: Alumina Block;
Al2O3: 48%~85%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Refractoriness: Sk35, Sk36, Sk37, Sk38, Sk40;
Apparent Porosity: 20-23%;
Bulk Density: 2.25-2.65g/cm3;
Refractoriness Under [email protected]: 1380-1550;
Thermal Linear Expansion@1000deg: 0.6%;
Fe2o3: 1.8-2.0%;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Pressing Process;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Al2O3: 55-80%;
Fe2o3: 1.5-2.5%;
Bulk Density: 2.25-2.80 g/cm3;
Apparent Porosity: 16-24;
Certifiacte: ISO9001, CE, etc;
Cold Crushing Strength: 45-100 MPa;
Working Temperature: 1450~1700ºC;
Application: Industrial Furnace;
Thermal Shock Resistance: Excellent;
Refractoriness: Ha55/Ha65/Ha70/Ha75/Ha80;
Refractoriness Under Load (0.2MPa): 1450-1700 ºC;
Color: Yellow/White;
Size Control: Accurate;
Production Time: 15-30 Days;
Testing Laboratory: Support;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Pressing Process;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Al2O3: 55-80%;
Fe2o3: 1.5-2.5%;
Bulk Density: 2.25-2.80 g/cm3;
Apparent Porosity: 16-24;
Certifiacte: ISO9001, CE, etc;
Cold Crushing Strength: 45-100 MPa;
Working Temperature: 1450~1700ºC;
Application: Industrial Furnace;
Thermal Shock Resistance: Excellent;
Refractoriness: Ha55/Ha65/Ha70/Ha75/Ha80;
Refractoriness Under Load (0.2MPa): 1450-1700 ºC;
Color: Yellow/White;
Size Control: Accurate;
Production Time: 15-30 Days;
Testing Laboratory: Support;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Pressing Process;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Al2O3: 55-80%;
Fe2o3: 1.5-2.5%;
Bulk Density: 2.25-2.80 g/cm3;
Apparent Porosity: 16-24;
Certifiacte: ISO9001, CE, etc;
Cold Crushing Strength: 45-100 MPa;
Working Temperature: 1450~1700ºC;
Application: Industrial Furnace;
Thermal Shock Resistance: Excellent;
Refractoriness: Ha55/Ha65/Ha70/Ha75/Ha80;
Refractoriness Under Load (0.2MPa): 1450-1700 ºC;
Color: Yellow/White;
Size Control: Accurate;
Production Time: 15-30 Days;
Testing Laboratory: Support;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Pressing Process;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Al2O3: 55-80%;
Fe2o3: 1.5-2.5%;
Bulk Density: 2.25-2.80 g/cm3;
Apparent Porosity: 16-24;
Certifiacte: ISO9001, CE, etc;
Cold Crushing Strength: 45-100 MPa;
Working Temperature: 1450~1700ºC;
Application: Industrial Furnace;
Thermal Shock Resistance: Excellent;
Refractoriness: Ha55/Ha65/Ha70/Ha75/Ha80;
Refractoriness Under Load (0.2MPa): 1450-1700 ºC;
Color: Yellow/White;
Size Control: Accurate;
Production Time: 15-30 Days;
Testing Laboratory: Support;
|