Specification |
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Bulk Density(g/cm3): 3.0-3.1g/cm3;
Al2O3: 90-92%;
Cr2o3: 4-7%;
MGO: 4-7%;
Cold Crushing Strength: 90-100MPa;
Modulus of Repture: 17-20MPa;
Air Permeability (N/Min): 200-650;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Application Area: Preheating Zone in Rotary Kiln;
Size: Customer Made;
Bulk Density: 2.3-2.35g/cm3;
Apparent Porosity: 15%;
Tsr 950ºC: 15cycle;
Rul: 1500;
CCS MPa: 80;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magnesia-Hecynite;
Application Area: Sintering Zone in Rotary Kiln;
Size: Customer Made;
Bulk Density: 2.9-3.0g/cm3;
Apparent Porosity: 17%;
Tsr 950ºC: 100 Cycle;
Rul: 1650-1700ºC;
CCS MPa: 60;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magnesia-Alumina;
size: B622 B322 B425 B825;
Lead time: 30-60days;
Shape standard: VDZ,ISO;
Service: Turn key project;
Life time: 1-2years;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Long Time Materials, Instant Materials;
Type: Refractory Material, Ceramic Crucible;
Shape: Crucible, Conical, Circular, Cylindrical;
Material: Alumina Cement, Clay, Clay;
Refractoriness: 1580< Refractoriness< 1770;
Color: White, Light Yellow;
Name: Ceramic Clay Fire Assay Crucible for Lab;
Max. Working Temperature: 1650 Degree Celsius;
Item: Ceramic Crucible;
Application: Thermal Analysis or Firing;
Capacity: 10ml, 20ml, 30ml, 50ml, 80ml, 100ml, 200ml, 500ml;
Purpose: Gold Smelting and Assaying;
Size: 30g, 40g, 45g, 50g, 65g;
Usage: Melting, Assaying;
Refractoriness Under Load: 1420 Degree Celsius;
Packing: Wooden Packing, Paper Carton Packing;
|